We report microwave magnetoabsorption (P) at room temperature in R0.6Sr0.4MnO3 (R = Pr and Nd) samples. P as a function of dc magnetic field (-2.5 kOe to +2.5 kOe) was measured for a broad frequency range (f = 0.1 - 4 GHz) of microwave…
We show that ac magnetoresistance at room temperature in La0.7Sr0.3MnO3 is extremely high (= 47% in H = 100 mT, f = 3-5 MHz), and magnetic field dependence of reactance exhibits a double peak behavior. However, magnitudes of the ac…
Employing a broadband microwave reflection configuration, we have measured the complex surface impedance, $Z_S(\omega,T,H)$, of single crystal La$_{0.8}$Sr$_{0.2}$MnO$_3$, as a function of frequency (0.045-45 GHz), temperature (250-325 K),…
We investigated temperature and magnetic field dependent radio-frequency electromagnetic absorption in La0.67Ba0.33MnO3 by monitoring changes in resonance frequency (fr) and current (II) through a LC resonant circuit powered by an…
The resistive and reactive parts of the magneto-impedance of sintered ferromagnetic samples of La0.7Sr0.3-xAgxMnO3 (x = 0.05, 0.25) have been measured at room temperature (<Tc) over frequency interval 1KHz to 15MHz and in presence of…
A single-phase polycrystalline La0.5Ba0.5CoO3-d sample was synthesized by microwave irradiation within 20 minutes of processing time and its structural, magnetic, electrical, and magnetostrictive properties were investigated. While the…
We have investigated magnetic field dependence of the ac magnetoresitance and the magnetoreactance in La0.67Ba0.33MnO3 over a wide frequency range from f = 0 to 30 MHz. A huge ac magnetoresistance of 55 % at f = 15 MHz in a small magnetic…
We report four probe impedance of La0.67Ba0.33MnO3 at f = 100 kHz under different dc bias magnetic fields. The ac resistance (R) exhibits a peak around Tp = 325 K which is accompanied by a rapid increase and a peak in the reactance (X) in a…
We report the detection of paramagnetic resonance in the double perovskite La2NiMnO6 at room temperature for microwave magnetic fields with frequencies, f = 1 GHz to 5 GHz, using two cavity-less methods. We use an indirect impedance method…
We report ac electrical transport in La0.7Sr0.3CoO3 and La1-xSrxMnO3 (x = 0.18- 0.5) as a function of temperature and frequency in H = 0 and 60 mT. Both resistive (R) and reactive (X) components of impedance (Z = R+jX) were measured. It is…
Magnetization has been measured for polycrystalline samples of LaCo1-xRhxO3 (0 {\leq} x {\leq} 0.9) in order to investigate magnetism induced in the solid solution of two nonmagnetic end phases of LaCoO3 and LaRhO3. It is found that a…
We report dynamical magnetotransport in a ferromagnetic metallic oxide, La0.7Sr0.3MnO3 using the ac impedance technique. The temperature dependence of the ac resistance(R) and the inductive reactance (X) of the complex impedance (Z = R+jX)…
Terahertz and far-infrared electric and magnetic responses of hexagonal piezomagnetic YMnO3 single crystals are investigated. Antiferromagnetic resonance is observed in the spectra of magnetic permeability mu_a [H(omega) oriented within the…
The dc magnetization (M) and electrical resistivity (\rho) as functions of magnetic field and temperature are reported for a series of lightly electron dopedCa(1-x)La(x)MnO(3) (0<=x<=0.10) specimens for which magnetization [Phys. Rev. B…
A theoretical study of magnetic field (h) effects on single-particle spectra and transport quantities of heavy fermion metals in the paramagnetic phase is carried out. We have employed a non-perturbative local moment approach (LMA) to the…
We report electrical, magnetic, magnetodielectric and magnetoabsorption properties of a polycrystalline GaFeO3. The resistivity measurement shows that the sample is highly insulating below 200 K and the resistivity above 200 K obey the…
Single crystals of Nd_{1-x}Pb_{x}MnO_{3} with x=0.2 are grown by high temperature solution growth technique using PbO-PbF_{2} flux. Magnetization studies on the samples show a transition to a ferromagnetic state below T_c ~ 125 K and the…
The results of dc magnetization, electrical and magnetoresistance and heat capacity measurements (2-300 K) on Tb7Rh3, crystallizing in Th7Fe3-type hexagonal structure, are reported. In this compound, magnetic ordering sets in around 90 K…
Neutron powder diffraction measurements, combined with magnetization and resistivity data, have been carried out in the doped perovskite La$_{1-x}$Ca$_x$MnO$_3$ ($x=0.47$, 0.50, and 0.53) to elucidate the structural, magnetic, and…
Systematic measurements of stress impedance (SI) and magneto-impedance (MI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at…