Related papers: Growth and transport properties under high pressur…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
Single crystals of MgB2 and Mg(B1-xCx)2 have been grown using cubic anvil technique. Tc values vary in a wide range (39-9 K) with carbon content varying from 0 up to 16%. Using SiC as the precursor leads to C and not to Si substituted…
Magnesium diboride crystals were grown with low melting alloy flux. The sample with superconductivity at 38.3 K was prepared in the zinc-magnesium flux and another sample with superconductivity at 34.11 K was prepared in the…
Superconductivity was discovered in a Ni0:05TaS2 single crystal. A Ni0:05TaS2 single crystal was successfully grown via the NaCl/KCl flux method. The obtained lattice constant c of Ni0:05TaS2 is 1.1999 nm, which is significantly smaller…
We demonstrated a pressure-induced phase transition from a low-Tc phase (3.5 K) to a high-Tc phase (8.7 K) in single crystalline PrO0.5F0.5BiS2. The high-Tc phase is easily observed even at 0.7 GPa by uniaxial pressure obtained from a…
Bulk single crystals of SrPt3P have been grown for the first time by a self-flux method at 2 GPa and 1500 {\deg}C using the cubic-anvil, high-pressure and high-temperature technique. The grown black crystals were found to have either a…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
Single crystals FeSe_x have been grown in evacuated sealed quartz tube using a NaCl/KCl flux. The products include two crystal structures of tetragon and hexagon. The electronic transport and magnetic properties measurements of FeSe_x…
We report on the first successful growth of single crystals of the noncentrosymmetric superconductor Mo$_3$Al$_2$C obtained by means of a cubic-anvil, high-pressure and high-temperature technique. Composition, structure, and normal-state…
Millimeter sized single crystals of CaFe$_{1-x}$Co$_x$AsF were grown using a self-flux method. It is found that high-quality single crystals can be grown from three approaches with different initial raw materials. The chemical compositions…
High-pressure superconductivity in a rare-earth doped Ca0.86Pr0.14Fe2As2 single crystalline sample has been studied up to 12 GPa and temperatures down to 11 K using designer diamond anvil cell under a quasi-hydrostatic pressure medium. The…
We report measurements of the transport and the magnetic properties of high-quality, sub-millimeter-sized MgB2 single crystals with clear hexagonal-plate shapes. The low-field magnetization and the magnetic hysteresis curves show the vortex…
We report the successful growth of high quality single crystals of LiFeAs with lateral sizes up to 5 x 5 mm2 by the Sn-flux method. Electrical resistivity studies reveal that the superconducting onset temperature is 18.2 K with a transition…
NbBiCh$_3$ (Ch = S, Se) misfit-layered superconducting single crystals were successfully grown using a CsCl/KCl flux for the first time. The obtained crystals had a well-developed habit parallel to the c-plane with a typical width of 1-2 mm…
The high anisotropy in RO1-aFaBiS2 (R denotes a rare-earth element) superconductors demonstrates their potential use as intrinsic Josephson junctions, considering the weak coupling among BiS2-PrO(F)-BiS2…
Single crystals of MgB2 have been grown with a high-pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB9 ternary nitride. The crystals are of a size up to 2x1x0.1mm3 with a weight up to 230 micrograms.…
Millimeter sized single crystals of KCa_2Fe_4As_4F_2 were grown using a self-flux method. The chemical compositions and crystal structure were characterized carefully. Superconductivity with the critical transition T_c = 33.5 K was…
We demonstrate direct evidence of possible surface superconductivity on small, well-shaped MgB2 single crystals. Transport measurements in the range H < 1.6 Hc2^c, where Hc2^c is the bulk upper critical field for the c axis, show non-Ohmic…
By means of high-pressure resistivity measurements on single crystals, we investigate the charge transport properties of Cu$_x$PdTe$_2$, notable for the combination of topological type-II Dirac semimetallic properties with superconductivity…
We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting…