The effects of isovalent doping on the superconducting transition temperature Tc in novel 112-type iron arsenide Ca1-xLaxFeAs2 were studied by conducting measurements of electrical resistivity rho and magnetization M. P or Sb doping…
The effects of simultaneous Sb doping on the superconductivity of 112-type Ca1-xRExFeAs2 (RE = La, Ce, Pr, and Nd) were studied through measurements of the magnetization and electrical resistivity. In Sb-free materials, the superconducting…
We report superconductivity in the novel 112-type iron-based compound Ca1-xLaxFeAs2. Single-crystal X-ray diffraction analysis revealed that the compound crystallizes in a monoclinic structure (space group P21), in which Fe2As2 layers…
We study antimony doping effects in the iron-based superconductor CaFe(Sb$_{x}$As$_{1-x}$)$_{2}$ by using the first-principle calculation. The calculations reveal that the substitution of the doped antimony atom into As of the chainlike As…
Arsenic doping in silicides has been much less studied compared with phosphorus. In this study, superconductivity is successfully induced by As doping in Mo$_5$Si$_3$. The superconducting transition temperature ($T_c$) reaches 7.7 K, which…
Superconducting transition temperature (Tc) reported in SnAs-based layered compound NaSn$_2$As$_2$ varies from 1.2 to 1.6 K, implying that its superconductivity is critically sensitive to non-stoichiometry. Here, we demonstrate that…
In this paper we report the superconductivity above 40 K in the electron doping single crystal Ca1-xRexFe2As2 (Re = La, Ce, Pr). The x-ray diffraction patterns indicate high crystalline quality and c-axis orientation. the resistivity…
We report the antimony (Sb) doping effect in a prototype system of iron-based supercon-ductors LaFeAsO1-yFy (y=0, 0.1, 0.15). X-ray powder diffraction indicates that the lattice pa-rameters increase with Sb content within the doping limit.…
In this paper we report the synthesis of iron-based superconductors CaFe2-xRhxAs2 using one-step solid state reaction method, which crystallizes in the ThCr2Si2-type structure with a space group I4/mmm. The systematic evolution of the…
BaFe2As2 is the parent compound of the '122' iron arsenide superconductors and crystallizes with the tetragonal ThCr2Si2 type structure, space group I4/mmm. A spin density wave transition at 140 K is accompanied by a symmetry reduction to…
The 1111-type iron-based superconductor LnFeAsO1-xFx (Ln stands for lanthanide) is the first material with a Tc above 50 K, other than cuprate superconductors. Electron doping into LaFeAsO by H, rather than F, revealed a double-dome-shaped…
A wide-range doping was achieved by a high-pressure method for TbFeAsO1-x from "under doped" to "over doped" superconducting compositions throughout the optimized superconductivity (Tc of 44 K). Tc vs. lattice constant shows a dome-shaped…
In the electron doped compounds SrFe_(2-x)Co_xAs_2 superconductivity with T_c up to 20 K is observed for 0.2 < x < 0.4. Results of structure determination, magnetic susceptibility, electrical resistivity, and specific heat are reported. The…
By using solid state reaction method we have fabricated the hole doped $La_{1-x}Sr_xFeAsO$ superconductors with Sr content up to 0.13. It is found that the sharp anomaly at about 150 K and the low temperature upturn of resistivity are…
Using one-step solid state reaction method, we have successfully synthesized the superconductor SrFe1-xRuxAs. X-ray diffraction indicates that the material has formed the ThCr2Si2-type structure with a space group I4/mmm. The systematic…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
Following the discovery of superconductivity in an iron-based arsenide LaO1-xFxFeAs with a superconducting transition temperature (Tc) of 26 K[1], Tc was pushed up surprisingly to above 40 K by either applying pressure[2] or replacing La…
Superconductivity was achieved in Ti-doped iron-arsenide compound Sr4Cr0.8Ti1.2O6Fe2As2 (abbreviated as Cr-FeAs-42622). The x-ray diffraction measurement shows that this material has a layered structure with the space group of…
Single crystals of mixed alkaline earth metal iron arsenide materials of Ba1-xSrxFe2As2 and Ba0.5Sr0.5(Fe1-yCoy)2As2 are synthesized via the self-flux method. Ba1-xSrxFe2As2 display spin-density wave features (TN) at temperatures…
Two novel 112-type palladium doped iron arsenides were synthesized and identified using comprehensive studies involving synchrotron x-ray diffraction and x-ray absorption near edge structure (XANES) experiments. Whereas in-plane arsenic…