Related papers: Effects of Iodine Annealing on Fe1+yTe0.6Se0.4
Oxygen annealing dramatically improved the superconducting properties of solid-state-reacted FeTe0.8S0.2, which showed only a broad onset of superconducting transition just after the synthesis. The zero resistivity appeared and reached 8.5…
To explore the origin of the unusual non-bulk superconductivity with a Tc up to 49 K reported in the rare-earth-doped CaFe2As2 , the chemical composition, magnetization, specific heat, resistivity, and annealing effect are systematically…
Resistivity, magnetic susceptibility and heat capacity measurements are reported for single crystals of Fe1+yTexSe1-x grown via a modified Bridgeman method with 0 < y < 0.15, and x= 1, 0.9, 0.75, 0. 67, 0.55 and 0.5. Although resistivity…
The effect of annealing on the basal-plane electrical resistivity of the YBa$_2$Cu$_3$O$_{7-\delta}$ single crystals is studied in a broad range of oxygen contents. Within the framework of s-d scattering of electrons by phonons, an increase…
We show here that the yttrium is immiscible and precipitates with various sizes in the body centred cubic V$_{0.6}$Ti$_{0.4}$ alloy superconductor. The number and size of the precipitates are found to depend on the amount of yttrium added.…
New iron selenide superconductors by intercalating smaller-sized alkali metals (Li, Na) and alkaline earths using high-temperature routes have been pursued ever since the discovery of superconductivity at about 30 K in KFe2Se2, but all have…
Fe$_{1+y}$Te$_{1-x}$Se$_x$ is unique in their structural simplicity, consisting of only FeTe/Se layers, which is favorable for probing the mechanism of superconductivity. Recently, a topological surface superconductivity as well as the…
Phase diagrams of as-grown and O2-annealed FeTe1-xSex determined from magnetic susceptibility measurement were obtained. For as-grown samples, the antiferromagnetic order was fully suppressed in the range region x \geq 0.15, and weak…
A large and high-quality single crystal (Li0.84Fe0.16)OHFe0.98Se, the optimal superconductor of newly reported (Li1-xFex)OHFe1-ySe system, has been successfully synthesized via a hydrothermal ion-exchange technique. The superconducting…
A novel method to prepare bulk Fe(Se0.5Te0.5) samples is presented, based on a melting process and a subsequent annealing treatment. With respect to the standard sintering technique, it produces much more homogeneous and denser samples,…
The inherent existence of multi phases in iron oxide nanostructures highlights the significance of them being investigated deliberately to understand and possibly control the phases. Here, the effects of annealing at 250 0C with a variable…
We investigated the transport properties of Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystals with different amounts of excess Fe prepared by O$_2$ annealing. The O$_2$ annealing remarkably improves transport properties. In particular, a…
The properties of the MoSr2YCu2O8 materials are found to systematically change with the oxygen concentration determined by the sintering and annealing conditions. The as-prepared (asp) sample is anti-ferromagnetically (AFM) ordered at 16 K.…
The optical properties of the iron-chalcogenide superconductor K{0.8}Fe{2-y}Se2, with a critical temperature Tc = 31 K, have been measured over a wide frequency range in the a-b planes above and below Tc. The conductivity is incoherent at…
The temperature dependence of the ac susceptibility for single-crystalline Fe1.02Se has been measured at high pressures to 6.7 GPa. The superconducting transition temperature Tc displays a large increase from 7 K to 30 K in the two-phase…
High-quality single crystals of K0.8Fe2Se1.4S0.4 are successfully synthesized by self-flux method with the superconducting transition temperatures Tconset = 32.8 K and Tczero = 31.2 K. In contrast to external pressure effect on…
We report that (Ba,K)Fe2As2 superconductor (a transition temperature, Tc = 38 K) shows inverse Iron isotope effect (-0.18) (the sample including the larger atomic weight of Fe depicts higher Tc). Measurements of both temperature dependent…
Aliovalent rare earth substitution into the alkaline earth site of CaFe2As2 single-crystals is used to fine-tune structural, magnetic and electronic properties of this iron-based superconducting system. Neutron and single crystal x-ray…
Resistivity and dc magnetization measurements were performed for the polycrystalline Pr$_{0.5}$Ca$_{0.5}$Co$_{1-x}$Fe$_{x}$O$_{3-\delta}$ ($x$ = 0, 0.05, 0.10 and 0.15) samples. The as-fabricated samples exhibit ferromagnetic (FM)…
The appearance of superconductivity at ambient pressures in the undoped iron pnictide parent compound SrFe2As2 is studied experimentally using several techniques and approaches to aid in understanding the nature of this phase. Low…