Related papers: Growth of ultra thin vanadium dioxide thin films u…

The transverse magnetoresistance of thin films of the Diluted Magnetic Semiconductor Zn$_{1-x}$Co$_{x}$O:Al on glass was studied for temperatures in the range of 5 to 100 K. Measurements were made on thin films grown by rf magnetron…

We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…

We report on giant positive magnetoresistance effect observed in VOx thin films, epitaxially grown on SrTiO3 substrate. The MR effect depends strongly on temperature and oxygen content and is anisotropic. At low temperatures its magnitude…

Vanadium dioxide, a well-known Mott insulator, is a highly studied electronic material with promising applications in information processing and storage. While fully crystalline layers exhibit exceptional properties, such as a sharp and…

This paper reports on the deposition and photoluminescence of amorphous and crystalline thin films of zinc gallium oxide with Ga:Zn atomic ratio varied between 0.3 and 5.7. The films are prepared by reactive direct current magnetron…

In the present work, HfO2 thin film (100nm) has been deposited by sputtering technique and annealed at various temperatures ranging from 400 to 1000\degree (in step of 200 \degree) in O2 ambient for 10 min. The samples have been…

Lowering the operating temperature of Solid Oxide Fuel Cells (SOFCs) is essential for improving durability and enabling large scale commercialization. Mixed ionic-electronic conductors (MIECs) of the Ruddlesden-Popper family, such as…

Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…

Vanadium silicide (V$_3$Si) is a promising superconductor for integration with silicon-based electronics, however the interfacial growth kinetics have a strong influence on the resulting superconducting properties and are not yet fully…

Vanadium dioxide (VO2) as a phase-change material controls the transferred heat during phase transition process between metal and insulator states. At temperature above 68C, the rutile structure VO2 keeps the heat out and increases the IR…

Thin films of Co2MnSi have been grown on a-plane sapphire substrates from three elemental targets by dc magnetron co-sputtering. These films are single phase, have a strong (110) texture and a saturation magnetization of 4.95 uB/formula…

Low resistivity (~3-24 mOhm.cm) with tunable n- and p-type phase pure Cu2O thin films have been grown by pulsed laser deposition at 25-200 0C by varying the background oxygen partial pressure (O2pp). Capacitance data obtained by…

Aluminosilicate (Al-Si-O) thin films containing up to 31 at. % Al and 23 at. % Si were prepared by reactive RF magnetron co-sputtering. Mechanical and structural properties were measured by indentation and specular reflectance infrared…

Pristine vanadium dioxide (VO2), an insulator-to-metal transition (IMT) material, is grown via furnace oxidation followed by rapid thermal annealing with forming gas (5%H2/95%N2) which reduces surface over-oxides such as V2O5 formed during…

Here, we report the full-fledged journey towards the material synthesis and characterization of few-layered/thin WSe$_2$ using sputtered W-films on SiO$_2$/Si substrates followed by electrical studies under dark and illumination conditions.…

Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…

We report on the magnetic and structural properties of ferromagnetic-insulating La$_2$CoMnO$_6$ thin films grown on top of (001) STO substrates by means of RF sputtering technique. Careful structural analysis, by using synchrotron X-ray…

Thermochromic VO2 films were prepared by reactive DC magnetron sputtering onto heated sapphire substrates and were used to make 100-nm-thick samples that were 10 {\mu}m wide and 100 micron long. The resistance of these samples changed by a…

We experimentally demonstrate that a thin (~150 nm) film of vanadium dioxide (VO2) deposited on sapphire has an anomalous thermal emittance profile when heated, which arises due to the optical interaction between the film and the substrate…

We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…