We report on the structural, magnetic, and magnetocaloric properties of polycrystalline (La0.5Pr0.5)0.6Ba0.4MnO3 (LPBMO), which was fabricated by a conventional solid-state reaction method. LPBMO undergoes a second-order paramagnetic to…
The magnetocaloric effect (MCE) in the A-site ordered manganite NdBaMn2O6 is studied. The MCE in this compound has an anomalous behavior. In low magnetic fields, the abrupt transitions between direct and inverse magnetocaloric effect are…
The magnetocaloric effect of polycrystalline samples of pure and Y-doped dipolar spin ice Dy2Ti2O7 was investigated at temperatures from nominally 0.3 K to 6 K and in magnetic fields of up to 2 T. As well as being of intrinsic interest, it…
Three first order magnetic phase transitions (FOMT) have been detected at TCPr, TNinter and TCinter over the temperature range from 5 K to 340 K at fields up to 9 T in PrMn1.4Fe0.6Ge2, and the magnetocaloric effect (MCE) around these…
We investigate the magnetocaloric effect (MCE), relative cooling power (RCP) and crystalline structure in Sb substituted CrTe_{1-x}Sb_{x} (0 \leq x \leq 0.2) alloy. The Rietveld refinement of the XRD pattern of CrTe1-xSbx showed the…
The hydrostatic pressure is expected to be an effective knob to tune the magnetostructural phase transitions of hexagonal MMX alloy. In this study, magnetization measurements under hydrostatic pressure were performed on a MMX martensitic…
In an effort to understand the impact of nanostructuring on the magnetocaloric effect, we have grown and studied gadolinium in MgO/W(50 $\textrm{\AA}$)/[Gd(400 $\textrm{\AA}$)/W(50 $\textrm{\AA}$)]$_8$ heterostructures. The entropy change…
We report an experimental demonstration of the magnetoelectrocaloric effect (MECE) in multiferroic $\mathrm{GdFeO_3}$. The temperature of the magnetic material changes when an external electric field is suddenly changed. MECE is the largest…
Magnetic dc susceptibility between 1.5 and 800 K, ac susceptibility and magnetization, thermodynamic properties, temperature dependence of radio and audio-wave dielectric constants and conductivity, contact-free dielectric constants at…
We report on neutron diffraction, thermal expansion, magnetostriction, dielectric, and specific heat measurements on polycrystalline FeCr2S4 in external magnetic fields. The ferrimagnetic ordering temperatures $T_{\mathrm{C}}\approx 170$ K…
La-Fe-Si-based alloys are among the most application-ready magnetocaloric materials for room-temperature magnetic refrigeration. Powder metallurgy methods have been previously demonstrated to successfully produce structures with sub-mm…
Magnetic cooling based on the magnetocaloric effect is a promising solid-state refrigeration technology for a wide range of applications in different temperature ranges. Previous studies have mostly focused on near room temperature (300 K)…
We present the results of a comparative analysis of the magnetocaloric effect (MCE) in Pr0.7Sr0.2Ca0.1MnO3, through direct and indirect measurements, using experimentally measured magnetization, specific heat, magnetostriction, resistivity,…
The electrical resistivity, magnetization and heat-capacity behavior of the Gd-based compounds, Gd2Co2Al, Gd2Co2Ga and Gd7Rh3, ordering magnetically at TC= 78 K, TC= 76 K and TN= 140 K have been investigated as a function of temperature and…
A remarkable decrease of the structural transition temperature of MnNiSi from 1200 K to <300 K by chemically alloying it with MnFeGe results in a coupling of the magnetic and structural transitions, leading to a large magnetocaloric effect…
We experimentally investigate magnetocaloric effect for single crystals of MnTe altermagnet at the transition to the state with spontaneous spin polarization, i.e. well below the N\'eel temperature of MnTe. The isothermal magnetic entropy…
We report the detailed study of the magnetocaloric effect (MCE) in a dipolar-Heisenberg magnet LiGdF$_4$ using magnetization measurements performed on a single crystal sample. Entropy variation on isothermal demagnetization from the…
We report a large entropy change (DeltaS) below 300 K, peaking near TC= 220 K, due to isothermal change of magnetic field, for Gd4Co3, with a refrigeration capacity higher than that of Gd. Notably, the isothermal magnetization is…
The crystallographic and magnetic properties of the cleavable 4d3 transition metal compound a-MoCl3 are reported, with a focus on the behavior above room temperature. Crystals were grown by chemical vapor transport and characterized using…
Reactive single-step hot-pressing at 1473 K and 35 MPa for 4 h produces dense, bulk, near single-phase, low-cost and low-criticality Fe$_2$Al$_{1.15}$B$_2$ and Fe$_2$Al$_{1.1}$B$_2$Ge$_{0.05}$Ga$_{0.05}$ MAB samples, showing a second-order…