Related papers: Superconductivity at 3.85 K in BaPd2As2 with the T…
Here we report the synthesis and discovery of superconductivity in a novel ternary iridium-arsenide compound BaIr2As2. The polycrystalline BaIr2As2 sample was synthesized by a high temperature and high pressure method. Crystal structural…
Here we report the discovery of superconductivity in the ternary LaRu2As2 compound. The polycrystalline LaRu2As2 samples were synthesized by the conventional solid state reaction method. Powder X-ray diffraction analysis indicates that…
Heat capacity, magnetic susceptibility, NMR, and resistivity of SrNi2P2 single crystals are presented, illustrating a purely structural transition at 325 K with no magnetism. Bulk superconductivity is found at 1.4 K. The magnitude of the…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…
Here we report the preparation and superconductivity of the 133-type Cr-based quasi-one-dimensional (Q1D) RbCr3As3 single crystals. The samples were prepared by the deintercalation of Rb+ ions from the 233-type Rb2Cr3As3 crystals which were…
We report appearance of superconductivity at 5K in NdO0.5F0.5BiS2 and supplement the discovery [1] of the same in layered sulfide based ZrCuSiAs type compounds. The bulk polycrystalline compound is synthesized by conventional solid state…
Superconductivity is observed with critical temperature $T_{c}$ = 2.0 K in self-flux-grown single crystals of $CaBi_{2}$. This material adopts the $ZrSi_{2}$ structure type with lattice parameters a = 4.696(1) $\AA$, b = 7.081(2) $\AA$ and…
We investigate bulk superconductivity in a high-quality single crystal of Bi$_2$Pd ($\beta$-Bi$_2$Pd, space group; I4/mmm) at temperatures less than 5.4 K by exploring its electrical resistivity, magnetic susceptibility, and specific heat.…
Recently a new family of Cr-based A2Cr3As3 (A = K, Rb, Cs) superconductors were reported, which own a rare quasi-one-dimensional (Q1D) crystal structure with infinite (Cr3As3)2- chains and exhibit intriguing superconducting characteristics…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
We successfully synthesized the BaPt$_2$As$_2$ single crystals and studied their structural and physical properties at low temperatures. BaPt$_2$As$_2$ crystallizes in the CaBe$_2$Ge$_2$-type tetragonal structure (P4/nmm) at room…
Here we report the synthesis and superconductivity of a novel ternary compound LaPd2Bi2. Shiny plate-like single crystals of LaPd2Bi2 were first synthesized by high-temperature solution method with PdBi flux. X-ray diffraction analysis…
Superconductivity is observed with critical temperatures near 9K in the tetragonal compound Mo5PB2. This material adopts the Cr5B3 structure type common to supercondcuting Nb5Si3-xBx, Mo5SiB2, and W5SiB2, which have critical temperatures of…
The synthesis and crystallography, magnetic susceptibility chi, magnetization M, specific heat Cp, in-plane electrical resistivity rho and in-plane magnetic penetration depth measurements are reported for single crystals of APd2As2 (A = Ca,…
We report the synthesis and physical properties of single crystals of stoichiometric BaNi2As2 that crystalizes in the ThCr2Si2 structure with lattice parameters a = 4.112(4) \AA and c = 11.54(2) \AA. Resistivity and heat capacity show a…
We report the superconductivity of a new quaternary compound ThMo$_2$Si$_2$C, synthesized with the arc-melting technique. The compound crystallizes in a tetragonal CeCr$_2$Si$_2$C-type structure with cell parameters of $a$ = 4.2296 \r{A}and…
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…
Polycrystalline samples with nominal composition of Ba(Fe1-xIrx)2As2 (x=0.10, 0.15, and 0.20) were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), electrical resistivity, and magnetization measurements.…
Single crystals of SrFe2-xPtxAs2 (0 < x < 0.36) were grown using the self flux solution method and characterized using x-ray crystallography, electrical transport, magnetic susceptibility, and specific heat measurements. The…
High-pressure superconductivity in a rare-earth doped Ca0.86Pr0.14Fe2As2 single crystalline sample has been studied up to 12 GPa and temperatures down to 11 K using designer diamond anvil cell under a quasi-hydrostatic pressure medium. The…