Plate-like single crystals of SrFe2As2 as large as 3x3x0.5 mm3 have been grown out of Sn flux. The SrFe2As2 single crystals show a structural phase transition from a high temperature tetragonal phase to a low temperature orthorhombic phase…
We report the discovery of a first-order phase transition at around 125 K in NbCrP, which is a nonsymmorphic crystal with Pnma space group. From the resistivity, magnetic susceptibility, and nuclear magnetic resonance measurements using the…
SrPt$_2$As$_2$ single crystals with CaBe$_2$Ge$_2$-type structure were synthesized by self-melting technique. X-ray diffraction, transmission electron microscopy, electrical resistivity, specific heat and optical spectroscopy measurements…
Single crystals of XPt$_{5}$P (X = Al, Ga, and In) were grown from a Pt-P solution at high temperatures, and ambient-pressure measurements of temperature-dependent magnetization, resistivity, and X-ray diffraction were made. Also, the…
We report structural and physical properties of the single crystalline ${\mathrm{Ca}}{\mathrm{Mn}}_{2}{\mathrm{P}}_{2}$. The X-ray diffraction(XRD) results show that ${\mathrm{Ca}}{\mathrm{Mn}}_{2}{\mathrm{P}}_{2}$ adopts the trigonal…
Heat capacity, magnetic susceptibility, NMR, and resistivity of SrNi2P2 single crystals are presented, illustrating a purely structural transition at 325 K with no magnetism. Bulk superconductivity is found at 1.4 K. The magnitude of the…
Millimeter sized single crystals of Mo3Sb7 are grown using the self-flux technique and a thorough characterization of their structural, magnetic, thermal and transport properties is reported. The structure parameters for the…
We report a room-temperature optical reflectivity study performed on [112]-oriented Cd$_3$As$_2$ single crystals over a broad energy range under external pressure up to 10 GPa. The abrupt drop of the band dispersion parameter…
We report on the crystal and magnetic structures, magnetic, and transport properties of SrMnSb$_2$ single crystals grown by the self-flux method. Magnetic susceptibility measurements reveal an antiferromagnetic (AFM) transition at $T_{\rm…
Single crystals of EuPd2Sb2 have been grown from PdSb self-flux. The properties of the single crystals have been investigated by x-ray diffraction, magnetic susceptibility chi, magnetization M, electrical resistivity rho, Hall coefficient…
Bulk single crystals of manganese phosphide (MnP) were grown from melt at 1 GPa and 1200 C by using a cubic-anvil, high-pressure, and high-temperature technique. The obtained black colored crystals exhibit a plate-like morphology, with flat…
Off-stoichiometric Ni$_2$MnIn Heusler alloys have drawn recent attention due to their large magnetocaloric entropy change associated with the first-order magneto-structural transition. Here we present crystal structural, calorimetric and…
The large single crystals of SrSnP were prepared using Sn self-flux method. The superconductivity in the tetragonal SrSnP is observed with the critical temperature of ~2.3 K. The results of a crystallographic analysis, superconducting…
High-temperature and high-pressure experiments were conducted on columbite-type ZnNb2O6, reaching temperatures up to 873 K at ambient pressure and pressures up to 30 GPa at ambient temperature, respectively. Through systematic analysis…
Synchrotron x-ray powder diffraction measurements have been performed on unpoled ceramic samples of (1-x)PbMg(1/3)Nb(2/3)O3-xPbTiO3 (PMN-xPT) with 30%<= x<= 39% as a function of temperature around the morphotropic phase boundary (MPB),…
ThCr2Si2-type intermetallic compounds are known to exhibit superelasticity associated with structural transitions through lattice collapse and expansion. These transitions occur via the formation and breaking of Si-type bonds, respectively,…
Resistivity measurements are widely exploited to uncover electronic excitations and phase transitions in metallic solids. While single crystals are preferably studied to explore crystalline anisotropies, these usually cancel out in…
We present thermodynamic, structural and transport measurements on Ba(Fe0.973Cr0.027)2As2 single crystals. All measurements reveal sharp anomalies at ~ 112 K. Single crystal x-ray diffraction identifies the structural transition as a first…
The purpose of the present work is to report studies on structural phase transition for PMN-xPT single crystal, with melt PbTiO3 composition around the MPB (x = 0.35 mol %), using infrared spectroscopy technique. The study was centered on…
The electrical conductivity and Raman spectroscopy measurements have been performed on MoS$_2$ at high pressures up to 90 GPa and variable temperatures down to 5 K. We find that the temperature dependence of the resistance in a metallic…