We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…
The recently discovered iron-based superconductors with very high upper critical field and small anisotropy have been regarded as a potential candidate material for high field applications. However, enhancements of superconducting…
We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The…
The high upper critical field and low anisotropy of iron-based superconductors make them being particularly attractive for high-field applications. However, the current carrying capability needs to be enhanced by overcoming the weak-link…
We report the realization of grain alignment in Sn-added Sr1-xKxFe2As2 superconducting tapes prepared by ex-situ powder-in-tube method. At 4.2 K, high transport critical current densities Jc of 2.5x10^4 A/cm^2 (Ic = 180 A) in self-field and…
Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament…
We report significant transport critical currents firstly achieved in Sr0.6K0.4Fe2As2 wires and tapes with a Tc = 34 K, which were fabricated through an in-situ powder-in-tube process. Silver was used as a chemical addition as well as a…
We report on the preparation of dense monofilamentary MgB2/Ni and MgB2/Fe tapes with high critical current densities. In annealed MgB2/Ni tapes, we obtained transport critical current densities as high as 2.3*105 A/cm2 at 4.2 K and 1.5 T,…
From the application point of view, large critical current densities Jc (H) for superconducting wires are required, preferably for magnetic fields higher than 5 T. Here we show that strong c-axis textured Sr1-xKxFe2As2 tapes with nearly…
We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of…
We report large transport critical current densities observed in Ag-added (Ba,K)Fe2As2 superconducting wires prepared by an ex-situ powder-in-tube (PIT) process. The wire has a simple composite structure sheathed only by Ag. A precursor…
We report the temperature dependence of the transport critical current density (Jc) in textured Sr1-xKxFe2As2/Fe (Sr122) tapes fabricated by an ex situ powder-in-tube process. Critical currents were measured in magnetic fields up to 0-15 T…
(Ba,K)Fe2As2 superconducting wires and tapes are fabricated by using hot isostatic pressing (HIP) technique, and their superconducting properties are studied. In the HIP round wire, transport critical current density (Jc) at 4.2 K has…
122 type pnictide superconductors are of particular interest for high-field applications because of their large upper critical fields Hc2 (> 100 T), low Hc2 anisotropy r (< 2), and high thin-film critical current densities Jc (> 1 MA/cm2 at…
Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly…
The c-axis textured Sr1-xKxFe2As2 tapes produced by cold rolling and post-annealing, could carry a high super-current over 2*104 A/cm2. However, the magnitude is far from its maximum, because of the current obstacles associated with various…
We demonstrate a large enhancement of critical current density (Jc) up to 1.0x10^7 A/cm2 at 5 K under self-field in (Ba,K)Fe2As2 single crystals by irradiating 320 MeV Au ions. With the very promising potential of this material in mind, we…
Improving transport current has been the primary issue for practical application of superconducting wires and tapes. However, the porous nature of powder-in-tube (PIT) processed iron-based superconducting tapes is thought to be one of the…
Multifilamentary MgB2/Fe wires and tapes with high transport critical current densities have been fabricated using a straightforward powder-in-tube (PIT) process. After annealing, we measured transport jc values up to 1.1 * 105 A/cm2 at 4.2…
MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density…