The lifetime of moving metallic components is often limited by accelerated oxidation. Yet, the mechanisms and pathways for oxidation during tribological loading are not well understood. Using copper as a model system, tribologically-induced…
We obtain the Paris law of fatigue crack propagation in a disordered solid using a fuse network model where the accumulated damage in each resistor increases with time as a power law of the local current amplitude. When a resistor reaches…
A microstructure-based model that accounts for the effect of grain size has been developed to study the effect of grain size on the fatigue life of Inconel 718 alloys. The fatigue behavior of two alloys with different grain size was…
The dislocation structures appearing in highly mis-oriented soft/hard grain pairs in near-alpha titanium alloy Ti6242Si were examined with and without the application of load holds (dwell) during fatigue. Dislocation pile-up in a soft grain…
This work presents a comprehensive investigation of the elastic and fracture behavior of ply-to-ply angle interlock three-dimensional woven composites. The research investigated novel splitting and wedge-driven out-of-plane fracture tests…
Accurate prediction of fracture toughness under complex loading conditions, like mixed mode I/II, is essential for reliable failure assessment. This paper aims to develop a machine learning framework for predicting fracture toughness and…
Molecular dynamics (MD) simulations have been performed to investigate the fatigue deformation behaviour of polycrystalline Cu with grain size of 5.4 nm. The samples were prepared using Voronoi algorithm with random grain orientations.…
A new method of combined loading was developed for manufacturing large - scale ingot of alpha-beta titanium alloy Ti-6Al-4V with the diameter of the gauge 120 mm and the length 300 mm. The process includes torsion with simultaneous tensile…
Nanocrystalline metals typically have high fatigue strengths, but low resistance to crack propagation. Amorphous intergranular films are disordered grain boundary complexions that have been shown to delay crack nucleation and slow crack…
The fractocohesive length - the ratio between fracture toughness and work-to-fracture - provides a material-specific length scale that characterizes the size-dependent fracture behavior of pristine elastomers. However, its relevance to…
We investigate the influence of microstructural traps in hydrogen-assisted fatigue crack growth. To this end, a new formulation combining multi-trap stress-assisted diffusion, mechanism-based strain gradient plasticity and a hydrogen- and…
We introduce a class of models based on near crack tip degradation of materials that can account for fracture growth under cyclic loads below the Griffith threshold. We incorporate the gradual degradation due to a cyclic load through a flow…
Fatigue crack advance induced by the application of cyclic quasistatic loads is investigated both numerically and analytically using a lattice spring model. The system has a quasi-one-dimensional geometry, and consists in two symmetrical…
The uniaxial tensile test response of a H decorated $\Sigma$ 5 [100] twist grain boundary (GB) in face-centered-cubic Al has been examined with first principles. The impurity shows a strong tendency to relocate during loading. To capture…
The evolution of a crack front under mixed mode loading (I+III) is studied using a phase field model in 3 dimensions with no stress boundary conditions. As previously observed experimentally in gels, there is a relaxation toward a geometry…
The galling behaviour of 316L stainless steel was investigated in both the unoxidised and oxidised states, after exposure in simulated PWR water for 850 hours. Galling testing was performed according to ASTM G196 in ambient conditions. 316L…
Fracture behavior in nickel-titanium (NiTi) shape memory alloys (SMAs) subjected to mode-I, isothermal loading is studied using finite element analysis (FEA). Compact tension (CT) SMA specimen is modeled in Abaqus finite element suite and…
High-entropy alloys (HEAs) refer to alloys composed of five or more elements in equal or near-equal amounts or in an atomic concentration range of 5 to 35 atomic percent (at%). Different elemental ratios will affect the microstructures of…
Fatigue failure can be thought by studying the collective motions of defects inside materials instead of focusing on the growth of a pre-existing micro-crack. An experimental study of the statistical distribution of acoustic emissions…
A planar crack generically segments into an array of "daughter cracks" shaped as tilted facets when loaded with both a tensile stress normal to the crack plane (mode I) and a shear stress parallel to the crack front (mode III). We…