The ferrimagnetic spinel $\mathrm{CoV_2O_4}$ has been a topic of intense recent interest, both as a frustrated insulator with unquenched orbital degeneracy and as a near-itinerant magnet which can be driven metallic with moderate applied…
We present X-ray diffraction (XRD), M\"ossbauer spectroscopy (MS) and d.c. magnetization measurements performed on ball-milled CuFe2O4 samples. The average particle size <d> was found to decrease to the nanometer range after t=15 min of…
Nanoparticles of Cr3+-substituted Ni-Zn ferrites with a general formula Ni0.4Zn0.6-xCrxFe2O4 (x = 0.0 - 0.6) have been synthesized via a facile microwave combustion route. The crystalline phase has been characterized by XRD, TEM, FT-I and…
Cobalt substitutions were investigated in Ni0.4Zn0.4Cu0.2Fe2O4 ferrites, initial complex permeability was then measured from 1 MHz to 1 GHz. It appears that cobalt substitution led to a decrease in the permeability and an increase in the…
Ferrimagnetic spinel materials of formula AB2X4, where A and B are transition metals and X is oxygen or sulphur, hold promise for the realization of multiferroic characteristics. In this work, we report synthesis of spinel CoMn2O4 and…
The Raman spectra of single crystals of NiFe2O4 were studied in various scattering configurations in close comparison with the corresponding spectra of Ni0.7Zn0.3Fe2O4 and Fe3O4. The number of experimentally observed Raman modes exceeds…
The non-equilibrium cation site occupancy in nanosized zinc ferrites (6-13 nm) with different degree of inversion (0.2 to 0.4) was investigated using Fe and Zn K-edge x-ray absorption spectroscopy XANES and EXAFS, and magnetic measurements.…
We prepared three ferrite nanocatalysts: (i) copper ferrite (CuFe2O4), (ii) ferrite where cobalt was substituted by nickel (NixCo1-xFe2O4, with x= 0, 0.2, 0.4, 0.6), and (iii) ferrite where nickel was substituted by zinc (ZnyNi1-yFe2O4 with…
In this study, a series of nanocrystalline ferrites of Ni0.7Cu0.30AlxFe2-xO4 (x=0.00 to 0.10 with a step of 0.02) has been synthesized through the sol-gel auto combustion technique. The structural, morphological, dielectric, and electrical…
The nanoparticles (NPs) of Zn1-xCuxFe2O4 (ZCFO) spinels with x = 0, 0.2, 0.4, 0.6 and 0.8 were synthesized by a sol-gel combustion method using acetate precursor. The NPs of ZCFO were prepared by following calcination process at 600C for…
A method of preparing the nanoparticles of CaCu3Ti4O12 (CCTO) with the crystallite size varying from 30 to 200 nm is optimized at a temperature as low as 680 1C from the exothermic thermal decomposition of an oxalate precursor,…
We report the magnetic properties of mechanically milled Co$_{0.2}$Zn$_{0.8}$Fe$_2$O$_4$ spinel oxide. After 24 hours milling of the bulk sample, the XRD spectra show nanostructure with average particle size $\approx$ 20 nm. The as milled…
The nucleation, crystallization, and growth mechanisms of MnFe2O4, CoFe2O4, NiFe2O4, and ZnFe2O4 nanocrystallites prepared from coprecipitated transition metal (TM) hydroxide precursors treated at sub-, near-, and supercritical hydrothermal…
Structural properties of CuAl$_{2}$O$_{4}$, which was recently argued to show unusual suppression of the Jahn-Teller distortions by the spin-orbit coupling, are investigated under pressures up to 6 GPa. Analysis of X-ray powder diffraction…
The structural distortions, orbital correlations, and electronic states in cobalt ferrite (CoFe2O4) were investigated using complementary characterisation techniques, including SR-XRD, HAXPES, XANES, EXAFS, and Raman spectroscopy. SR-XRD…
The reflectivity of single-crystalline CoO has been studied by optical spectroscopy for wave numbers ranging from 100 to 28,000\wn and for temperatures 8 $< T <$ 325 K\@. A splitting of the cubic IR-active phonon mode on passing the…
Spinel chromites ACr$_2$O$_4$ with inherent magnetic geometrical frustration usually exhibit a noncollinear ferrimagnetic ground state when A are magnetic ions, with possibly crystallite-size dependent intriguing magnetic features. Here, we…
We have investigated the structural, magnetic, thermodynamic, and dielectric properties of polycrystalline CoCr$_2$O$_4$, an insulating spinel exhibiting both ferrimagnetic and spiral magnetic structures. Below $T_c$ = 94 K the sample…
Ultrasound velocity measurements were performed on a single crystal of spin-frustrated ferrite spinel ZnFe$_2$O$_4$ from 300 K down to 2 K. In this cubic crystal, all the symmetrically-independent elastic moduli exhibit softening with a…
Single-phase Mg-doped ZnFe$_2$O$_4$ nanoparticles with x= 0, 0.3, 0.5, 0.7 have been prepared by the glycol-thermal method without any subsequent calcination. The crystallite size, microstructure and magnetic properties of the prepared…