Related papers: MgB2 bulk superconducting magnet
The magnetic field dependence of the spin-susceptibility, $\chi_{s}$ was measured in the superconducting state of high purity MgB$_{2}$ fine powders below 1.3 T. $\chi_{s}$ was determined from the intensity of the conduction electron spin…
The distribution of the current density and the profile of the trapped magnetic field of a superconducting disk magnetized by uniform field are calculated from first principles. The effect of the superconducting parameters is taken into…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
We report on measurements of the magnetic moment in superconducting MgB2 single crystals. We find \mu_0H_{c2}^c(0) = 3.2 T, \mu_0H_{c2}^{ab}(0) = 14.5 T, \gamma = 4.6, \mu_0H_c(0) = 0.28 T, and \kappa(T_c) = 4.7. The standard…
Electrical magnetoresistance and tunnel diode oscillator measurements were performed under external magnetic fields up to 41 T applied along the crystallographic b-axis (hard axis) of UTe$_2$ as a function of temperature and applied…
By means of new muon spin relaxation experiments, we disentangle extrinsic and intrinsic sources of low-temperature bulk magnetism in the candidate topological Kondo insulator (TKI) SmB6. Results on Al-flux grown SmB6 single crystals are…
We report here synthesis, structural, DC magnetization, and transport studies of new BiS2 based layered LaO0.5F0.5BiS2 superconductor [1]. The sample was synthesized by conventional solid state route via vacuum encapsulation technique at…
The specific heat C of a sintered polycrystalline sample of MgB2 with a bulk superconducting transition temperature Tc=36.7 K is measured as a function of the temperature (2-300 K) and magnetic field (0-16 T), together with magnetic…
Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in…
Superconducting Ag or Cu sheathed MgB2 wires have been fabricated by conventional powder-in-tube techniques. The in-situ reaction of Mg and B powders with atomic proportions of 1:2 and 1.33:2 inside Ag or Cu tubes at low temperatures have…
The increase of energy in accelerators over the past decades has led to the design of superconducting magnets for both accelerators and the associated detectors. The use of Nb-Ti superconducting materials allows an increase in the dipole…
Metastable calcium atoms, produced in a magneto-optic trap (MOT) operating within the singlet system, are continuously loaded into a magnetic trap formed by the magnetic quadrupole field of the MOT. At MOT temperatures of 3 mK and 240 ms…
Porous magnesium diboride samples have been prepared by the heat treatment of a pressed mixture of Mg and MgB2 powders. It was found that linked superconducting structure is formed down to the minimum normalized density gamma= d/do= 0.16…
Magnetization (M) and magnetoresistance (MR) measurements on polycrystalline R2Mn3Si5 (R = Tb, Dy and Ho) compounds (tetragonal, space group P4/mnc) have been carried out in the temperature range of 2 K-300 K, in various applied fields.…
MgB2 is a promising superconductor for important large-scale applications for both high field magnets and cryocooler-cooled magnet operated at temperatures around 20 K. In this work, by utilizing C60 as a viable alternative dopant, we…
The size effect of the raw B powder on the MgB2 phase formation has been studied by the technique of in-situ high temperature resistivity (HT-rT) measurement. The onset temperature, Tonset, and the completion temperature, TPF, of the phase…
The in situ annealing conditions of pulsed laser deposited MgB2 films were studied. The precursor films were deposited at 250 C from a stoichiometric MgB2 target in a 120mTorr Ar atmosphere. The films were then in situ annealed at a…
Thin films of the recently discovered magnesium diboride (MgB2) intermetalic superconducting compound have been grown using a magnetron sputtering deposition technique followed by in-situ annealing at 830 C. High quality films were obtained…
The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2…
We report resistivity and magnetization of single crystal MgB2, focusing on the broadening of superconducting (SC) transition in magnetic fields. In-plane and out-of-plane resistivity indicate that the broadening of superconducting…