Related papers: High Field (14Tesla) Magneto Transport of Sm/PrFeA…
Bulk polycrystalline samples, SmFeAsO and the iso-structural superconducting SmFeAsO0.80F0.20 are explored through resistivity with temperature under magnetic field {\rho}(T, H), AC and DC magnetization (M-T), and Specific heat (Cp)…
In this paper the magnetic behaviour of SmFeAsO and SmFeAs(O0.85F0.15) samples is presented and discussed. Molar susceptibility of SmFeAsO exhibits a local peak at T around 140K due to the establishment of a long range antiferromagnetic…
We report the synthesis and physical property characterization of PrFe1-xCoxAsO with x = 0.0 to 1.0. The studied samples are synthesized by solid state reaction route via vacuum encapsulation method. The pristine compound PrFeAsO does not…
Detailed magnetization and magneto-transport measurements studies are carried out to unearth the anomalous magnetism of Pr in PrCoAsO compound. The studied PrCoAsO sample is single phase and crystallized in the tetragonal structure with…
The superconducting and ground state samples of PrFeAsO0.8F0.2 and PrFeAsO have been synthesised via easy and versatile single step solid state reaction route. X-ray & Reitveld refine parameters of the synthesised samples are in good…
We report the magnetic field dependence of resistivity ($\rho$) and specific heat ($C$) for the non-superconducting PrFeAsO compound. Our study shows a hitherto unobserved anomaly at $T_{SR}$ in the resistivity and specific heat data which…
Superconductivity was achieved in PrFeAsO by partially substituting Pr^{3+} with Sr^{2+}. The electrical transport properties and structure of this new superconductor Pr_{1-x}Sr_xFeAsO at different doping levels (x = 0.05$\sim$ 0.25) were…
We present detailed magnetization and magneto-transport studies on the title compound SmCoAsO. In a recent paper we reported [1] the complex magnetism of this compound. SmCoAsO undergoes successive paramagnetic (PM) - ferro-magnetic (FM) -…
Correlation between structural/microstructural and magneto-thermal transport properties of FeAs-based SmFeAsO and SmFeAsO0.85F0.15 has been studied in detail. The Rietveld analysis of room temperature powder X-ray diffraction (XRD) data…
We have investigated the evolution of the low temperature specific heat anomaly (TN=5.4K in zero field) in polycrystalline SmFeAsO samples with magnetic fields up to 35T. The anomaly remains very sharp up to 16T and becomes rounded with…
Measurements of magnetization, specific heat, electrical resistivity, Hall effect, and magnetoresistance on single crystalline samples of LaFeAsO grown in a NaAs flux are reported. While this material is known to be a semimetal, the…
For the first time magnetrotransport of the ferromagnetic high-pressure phases of (GaSb)$_2$M (M=Cr,Mn) was measured. It was found that the main component of magnetotransport in these phases is negative and its amplitude is increasing with…
We present spin transport studies on a low-field, room-temperature magnetoelectric multiferroic polycrystalline $\text{Sr}_{3}\text{Co}_{2}\text{Fe}_{24}\text{O}_{41}$ (SCFO)|Pt heterostructure wherein a highly tunable transverse conical…
A high-quality PrFeAsO$_{1-\delta}$ single crystal ($T_{\rm c}=44$ K) has been investigated by the magnetic torque. Antiferromagnetism of the Pr$^{3+}$ ions was found to coexist with superconductivity in PrFeAsO$_{1-\delta}$ at temperatures…
The longitudinal electrical resistivity and the transverse Hall resistivity of CeFeAsO are simultaneously measured up to a magnetic field of 45T using the facilities of pulsed magnetic field at Los Alamos. Distinct behaviour is observed in…
Superconducting fluctuations (SF) in SmFeAsO$_{0.8}$F$_{0.2}$ (characterized by superconducting transition temperature $T_{c} \simeq 52.3$ K) are investigated by means of isothermal high-resolution dc magnetization measurements. The…
We present magnetization and specific heat data of a La5/3Sr1/3NiO4 single crystal in high magnetic fields. From the charge and spin stripe ordering temperatures, as well as a magnetic low temperature transition, we have constructed the…
The results of magnetization, heat-capacity, and electrical resistivity (rho) studies of the compounds, RMAs2 (R= Pr and Sm; M= Ag, Au), crystallizing in HfCuSi2-derived structure are reported. PrAgAs2 orders antiferromagnetically at T_N= 5…
We report the observation of an unusual $B$ dependence of transverse magnetoresistance (MR) in the PrFeAsO, one of the parent compound of pnictide superconductors. Below the spin density wave transition, MR is large, positive and increases…
Magnetotransport properties of p-InMnAs layers are studied in pulsed magnetic fields up to 30 T. Samples were prepared by the laser deposition and annealed by ruby laser pulses. Well annealed samples show p-type conductivity while they were…