Superconducting thick films (200$\mu$m-300$\mu$m) of YBCO have been fabricated successfully on MgO substrates by a new approach. The precursor powders (YBa2Cu3O7-$\delta$(Y123)+0.1molY2BaCuO5(Y211)) are placed between two MgO (10mm x 10mm)…
In the present work we study the growth by pulsed laser deposition of YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on the r-cut sapphire substrates. To improve the matching of the lattice parameters between the substrate and the film we use…
The temperature dependence of the relaxation dynamics in the bilayer thin film heterostructure composed of multiferroic BiFeO$_{3}$ (BFO) and superconducting YBa$_{2}$Cu$_{3}$O$_{7}$ (YBCO) grown on a (001) SrTiO$_{3}$ substrate is studied…
Much smoother surfaces and significantly improved superconducting properties of relatively thick YBa2Cu3O7 (YBCO) films have been achieved by introducing a multilayered structure with alternating main YBCO and additional NdBCO layers. The…
We report a simple and easily controllable method where a nano-undulated surface morphology of Nd1/3Eu1/3Gd1/3Ba2Cu3Ox (NEG) films leads to a substantial increase in the critical current density in superconducting YBa2Cu3Ox (YBCO) films…
We report the growth of NdBa2Cu3O7-d films on (100) MgO substrate by Molecular Beam Epitaxy (MBE). Large area NdBa2Cu3O7-d films with homogeneous superconducting properties were grown by precise control of stoichiometry and the optimisation…
Freestanding GdBa2Cu3O7 (GdBCO) superconducting thin films were fabricated using a water-soluble Sr3Al2O6 (SAO) sacrificial layer in combination with thermal release tape. An amorphous Al2O3 capping layer was introduced to suppress crack…
We have grown and characterized 30 nm thick YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films, deposited by pulsed laser deposition on both MgO (110) and SrTiO$_3$ (001) substrates, which induce opposite strain to the superconducting layer. By…
Y-Ba-Cu-O (YBCO) and Sm-Ba-Cu-O (SmBCO) thin films have been used for the first time as heterogeneous seeds to multi-seed successfully the melt growth of bulk YBCO in a multi-seeded melt growth (MSMG) process. The use of thin film seeds,…
We study the growth and electronic properties of a high temperature superconductor, YBa$_2$Cu$_3$O$_7$ (YBCO) in proximity of a magnetic material, La$_{0.67}$Sr$_{0.33}$MnO$_3$ (LSMO). High quality single crystalline films of YBCO and…
Epitaxial bilayers of ferromagnetic La2/3Ca1/3MnO3 (LCMO) and superconducting YBa2Cu3O7-d (YBCO) have been grown on single-crystalline SrTiO3 (STO) substrates by pulsed laser deposition. The Manganese magnetization profile across the FM…
Nb3Sn films were fabricated by multilayer sequential sputtering on Nb at substrate temperatures ranging from room temperature to 250 {\deg}C. The multilayers were then annealed inside a separate vacuum furnace at 950 {\deg}C for 3h. The…
This paper reports the nanoscale texture and microstructure of a high-performance NdFeAs(O,F) superconducting thin film grown by molecular beam epitaxy on a textured MgO/Y$_2$O$_3$/Hastelloy substrate. The NdFeAs(O,F) film forms a highly…
We have grown untwinned YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films on (110) MgO substrates that were pre-annealed at high temperature in oxygen atmosphere. The annealing results in surface reconstruction with shallow facets, which induce the…
Improved trapped fields are reported for bulk melt-textured YBa2Cu3O7-x (YBCO) material in the temperature range between 20 K and 50 K. Trapped fields up to 12.2 T were obtained at 22 K on the surface of single YBCO disks (with Ag and Zn…
YBa$_2$Cu$_3$O$_{7-\delta}$ is a good candidate to systematically study high-temperature superconductivity by nanoengineering using advanced epitaxy. An essential prerequisite for these studies are coherently strained…
The fabrication of free-standing ultra-thin films from high-temperature (high-Tc) superconductors is of great interest for the development of superconducting nanowire single-photon detectors with high operating temperatures. We successfully…
Epitaxial bilayers of the high-temperature-superconductor YBa2Cu3O7-d (YBCO) and the ferromagnetic metal La0.67Ca0.33MnO3 (LCMO) were prepared by pulsed laser deposition on (110)-oriented SrTiO3 substrates, such that the CuO2 planes of YBCO…
YBCO films were successfully prepared on biaxially textured Ag{110}<211> substrates by using pulsed laser deposition. X-ray diffraction results showed that the degree of preferential orientation of Ag{110}<211> substrates varied with…
Dissipation-free current transport in high-temperature superconductors is one of the most crucial properties of this class of materials which is directly related to the effective inhibition of flux line movement by defect structures. In…