We studied the magnetic and transport properties of Co nanoparticles (NPs) being capped with varying amounts of Pt. Beside field and temperature dependent magnetization measurements we performed delta-M measurements to study the magnetic…
Using microemulsion methods, CoO-Pt core-shell nanoparticles (NPs), with diameters of nominally 4 nm, were synthesized and characterized by high-resolution transmission electron microscopy (HRTEM) and a suite of x-ray spectroscopies,…
Magnetic nanoparticles are important building blocks for future technologies ranging from nano-medicine to spintronics. Many related applications require nanoparticles with tailored magnetic properties. However, despite significant efforts…
Spherical NiPt@C nanoalloys encapsulated in carbon shells are synthesized by means of high-pressure chemical vapour deposition. Upon variation of the synthesis parameters, both the alloy core composition and the particle size of the…
When the particle size of a metal is reduced, it is expected that an energy gap will open due to the quantum size effect. However, the energy gap in platinum (Pt) metal nanoparticles has not been observed directly by nuclear magnetic…
$^{195}$Pt-NMR measurements of Pt nanoparticles with a mean diameter of 4.0 nm were performed in a high magnetic field of approximately $\mu_0 H = 23.3$ T to investigate the low-temperature electronic state of the nanoparticles. The…
We report detailed studies on magnetic properties of Co3O4 nanoparticles of average size 12.5 nm. Temperature and field dependence of magnetization, wait time dependence of magnetic relaxation (aging), memory effects and temperature…
We study magnetic, transport and thermal properties of Cobalt carbide nanocomposite with a mixture of Co2C and Co3C phases in 1:1 ratio, with an average particle diameter of 40$\pm 15$ nm. We show that the behavior of the nanocomposite is…
The magnetic properties and magnetization dynamics of polycrystalline ultra-thin Co layers were investigated using a broadband ferromagnetic resonance (FMR) technique at room temperature. A variable thickness (1 nm $\leq t \leq$ 10 nm) Co…
The magnetic properties of thin-film Pd/Fe/Pd trilayers in which an embedded ~1.5 A-thick ultrathin layer of Fe induces ferromagnetism in the surrounding Pd have been investigated. The thickness of the ferromagnetic trilayer is controlled…
To evaluate the self-heating effects of FeCo magnetic nanoparticles, the surface oxidized FeCo nanoparticles were synthesized by co-precipitation method with the reduction reaction without any post treatments. As-synthesized FeCo…
ZnO nanoparticles with Wurtzite structure were prepared by chemical methods at low temperature in aqueous solution. Nanoparticles are in the range from about 10 to 30 nm. Ferromagnetic properties were observed from 2 K to room temperature…
We experimentally demonstrate the existence of magnetic coupling between two ferromagnets separated by a thin Pt layer. The coupling remains ferromagnetic regardless of the Pt thickness, and exhibits a significant dependence on temperature.…
We synthesized pure and Co-doped (6.25 12.5 at.) ZrO$_2$ nanopowders in order to study their magnetic properties.We analyzed magnetic behavior as a function of the amount of Co and the oxygenation, which was controlled by low pressure…
We studied the physical behavior of PdO nanoparticles at low temperatures, which presents an unusual behavior clearly related to macroscopic quantum tunneling. The samples show a tetragonal single phase with P42/mmc space group. Most…
Magnetization and Mossbauer studies have been performed on the polymer coated magnetite nanoparticles with particle size from 5.1 to 14.7 nm. The maximum in the temperature dependence of magnetization (TM) is found to be inconsistent with…
In this work, the structural and magnetic properties of the gold-coated FePt nanoparticles synthesized from high-temperature solution phase are presented. The amount of gold was optimized to obtain most of the FePt particles coated. The…
We report magnetic measurements up to 1100 K on a multi-walled carbon nanotube mat sample using a Quantum Design vibrating sample magnetometer. In an ultra-low field (H = -0.02 Oe), we find a very large paramagnetic susceptibility (up to…
Structural and magnetic properties of Fe@Pt core-shell nanostructure prepared by a sequential reduction process are reported. Transmission electron microscopy (TEM) shows nearly spherical particles fitting a lognormal size distribution with…
We report magnetic studies on gelatin coated NiO nanoparticles of average size 7 nm. Temperature and time dependence of dc magnetization, wait time dependence of magnetic relaxation (aging), memory effects in the dc magnetization and…