Related papers: Superconductivity in SrFe2As2 with Pt Doping
By substituting the Fe with the 5d-transition metal Ir in SrFe2As2, we have successfully synthesized the superconductor SrFe2-xIrxAs2 with Tc = 22.3 K at x = 0.5. X-ray diffraction indicates that the material has formed the ThCr2Si2-type…
Electrical resistivity under high pressure have been measured on nominally pure SrFe2As2 up to 14 GPa. The resistivity drop appeared with increasing pressure, and we clearly observed zero resistivity. The maximum of superconducting…
Single crystals of SrFe2-xPtxAs2 (0 < x < 0.36) were grown using the self flux solution method and characterized using x-ray crystallography, electrical transport, magnetic susceptibility, and specific heat measurements. The…
Using one-step solid state reaction method, we have successfully synthesized the superconductor SrFe1-xRuxAs. X-ray diffraction indicates that the material has formed the ThCr2Si2-type structure with a space group I4/mmm. The systematic…
By using solid state reaction method, we have synthesized the Pd-doped superconductor SrFe2-xPdxAs2. The systematic evolution of the lattice constants indicated that the Fe ions were successfully replaced by the Pd. By increasing the doping…
In the electron doped compounds SrFe_(2-x)Co_xAs_2 superconductivity with T_c up to 20 K is observed for 0.2 < x < 0.4. Results of structure determination, magnetic susceptibility, electrical resistivity, and specific heat are reported. The…
By substituting Fe with the 5d-transition metal Pt in BaFe2As2, we have successfully synthesized the superconductors BaFe2-xPtxAs2. The systematic evolution of the lattice constants indicates that the Fe ions were successfully replaced by…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…
Compounds of Sr1-xLaxFe2As2 were synthesized by solid state reaction at 1273 K, under pressures of 2 or 3 GPa. The Sr1-xLaxFe2As2 phase was dominant up to x = 0.5, and superconductivity was observed at $x \ge 0.2$. A maximum critical…
In this paper we report the synthesis of iron-based superconductors CaFe2-xRhxAs2 using one-step solid state reaction method, which crystallizes in the ThCr2Si2-type structure with a space group I4/mmm. The systematic evolution of the…
By doping Rh to the Fe sites in SrFe2As2, superconductivity is induced when the antiferromagnetic (AF) order is suppressed. The maximum superconducting transition temperature was found at about 22 K with the doping level of x = 0.25. It is…
We report resistivity measurement under pressure in single crystals of SrFe_2As_2, which is one of the parent materials of Fe-based superconductors. The structural and antiferromagnetic (AFM) transition of T_0 = 198 K at ambient pressure is…
We report a breakdown of the scaling of the antiferromagnetic transition temperature T_N on chemical doping for Pt-doped CaFe2As2. The substitution of Pt is ineffective in the reduction of antiferromagnetic ordering as well as in inducing…
Polycrystalline Sr1-xNdxFeAsF samples were prepared at various Nd-doping levels using both a stoichiometric mixture of the starting materials and in slight excess amounts of FeAs. Susceptibility and resistivity of the samples were studied…
Polycrystalline samples with nominal composition of Ba(Fe1-xIrx)2As2 (x=0.10, 0.15, and 0.20) were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), electrical resistivity, and magnetization measurements.…
The magnetism in SrFe2As2 can be suppressed by electron doping through a small substitution of Fe by Co or Ni, giving way to superconductivity. We demonstrate that a massive substitution of Fe by isovalent ruthenium similarly suppresses the…
Superconductivity has been explored in single crystals of the Ni-doped FeAs-compound SrFe2-xNixAs2 grown by self-flux solution method. The antiferromagnetic order associated with the magnetostructural transition of the parent compound…
We have synthesized the polycrystalline samples of Eu1-xKxFe2As2 (x = 0-1) and carried out systematic characterization using x-ray diffraction, ac & dc magnetic susceptibility, and electrical resistivity measurements. We have seen a clear…
High-pressure superconductivity in a rare-earth doped Ca0.86Pr0.14Fe2As2 single crystalline sample has been studied up to 12 GPa and temperatures down to 11 K using designer diamond anvil cell under a quasi-hydrostatic pressure medium. The…
A new hight Tc Fe-based compound system, AFe2As2 with A = K, Cs, K/Sr and Cs/Sr has been found. Through electron-doping, Tc of the A = K and Cs compounds rises to ~37 K, and finally enter a spin-density-wave state (SDW) through further…