The effect of pressure on superconductivity of 111 type NaxFeAs is investigated through temperature dependent electrical resistance measurement in a diamond anvil cell. The superconducting transition temperature (Tc) increases from 26 K to…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…
Exploring new unconventional superconductors is of great value for both fundamental research and practical applications. It is a long-term challenge to develop and study more hole-doped superconductors in 1111 system of iron-based…
A brief overview of changes in the superconducting transition temperature under pressure and evolution of specific heat capacity jump at Tc for two related families of iron - based superconductors, Ba{1-x}KxFe2As2 (0.2 < x < 1.0) and…
Superconductivity with zero resistance transition temperature (Tc) up to 8.4 K and 8.3 K can be obtained by doping cobalt and sodium in alfa-FeSe with the nominal composition of Fe0.92Co0.08Se and Na0.1FeSe, respectively. The electrical…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
Here we report bulk superconductivity in BaFe1.8Co0.2As2 single crystals below Tc = 22 K, as demonstrated by resistivity, magnetic susceptibility, and specific heat data. Hall data indicate that the dominant carriers are electrons, as…
A series of high quality NaFe$_{1-x}$Cu$_x$As single crystals has been grown by a self-flux technique, which were systematically characterized via structural, transport, thermodynamic, and high pressure measurements. Both the structural and…
We report pressure-induced superconductivity in a single crystal of CaFe2As2. At atmospheric pressure, this material is antiferromagnetic below 170 K but under an applied pressure of 0.69 GPa becomes superconducting, with a transition…
We report single-crystal growth of La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$ iron-based superconductor with the size of several millimeters. The samples were accidentally obtained in trying to grow LaFeAsO$_{1-y}$F$_y$ ( $y \geq$ 0.8 ) single…
In this letter, we report that the superconductivity transition temperature in beta-Fe1.01Se increases from 8.5 to 36.7 K under applied pressure of 8.9 GPa. It then decreases at higher pressure. A dramatic change in volume is observed at…
Resistivity and magnetic susceptibility measurements under external pressure were performed on single-crystals NaFe1-xCoxAs (x=0, 0.01, 0.028, 0.075, 0.109). The maximum Tc enhanced by pressure in both underdoped and optimally doped…
High-pressure superconductivity in a rare-earth doped Ca0.86Pr0.14Fe2As2 single crystalline sample has been studied up to 12 GPa and temperatures down to 11 K using designer diamond anvil cell under a quasi-hydrostatic pressure medium. The…
The observation of non-bulk superconductivity with an unexpectedly high onset transition temperature Tc up to ~ 49 K in non-superconducting single crystalline CaFe2As2 upon rare-earth doping has raised interesting questions concerning its…
A superconducting transition temperature Tc as high as 100 K was recently discovered in 1 monolayer (1ML) FeSe grown on SrTiO3 (STO). The discovery immediately ignited efforts to identify the mechanism for the dramatically enhanced Tc from…
As the simplest iron-based superconductor, FeSe forms a tetragonal structure with transition temperature Tc ~ 8 K. With assistance of pressure, or other techniques, Tc can be greatly enhanced, even to above liquid nitrogen temperature. The…
Resistivity, magnetic susceptibility and heat capacity measurements are reported for single crystals of Fe1+yTexSe1-x grown via a modified Bridgeman method with 0 < y < 0.15, and x= 1, 0.9, 0.75, 0. 67, 0.55 and 0.5. Although resistivity…
Single crystals of the compound LaFePO were prepared using a flux growth technique at high temperatures. Electrical resistivity measurements reveal metallic behavior and a resistive transition to the superconducting state at a critical…
Polycrystalline Sr1-xNdxFeAsF samples were prepared at various Nd-doping levels using both a stoichiometric mixture of the starting materials and in slight excess amounts of FeAs. Susceptibility and resistivity of the samples were studied…
Iron-arsenide superconductor Na$_{1-\delta}$FeAs is highly reactive with the environment. Due to the high mobility of Na ions, this reaction affects the entire bulk of the crystals and leads an to effective stoichiometry change. Here we use…