We report the temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition. The superconducting transition width for the resistivity measurement was about 0.4 K, and the low-field…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated in magnetic fields up to 16 T. The upper critical field of the major fraction of the investigated sample was determined…
Heat-capacity measurements of a 39 microgramm MgB_2 single crystal in fields up to 14 T and below 3 K allow the determination of the low-temperature linear term of the specific heat, its field dependence and its anisotropy. Our results are…
Single crystals of Mg1-xAlxB2 have been grown at a pressure of 30 kbar using the cubic anvil technique. Precipitation free crystals with x < 0.1 were obtained as a result of optimization of already developed MgB2 crystal growth procedure.…
We investigate the influence of carbon-ion irradiation on the superconducting critical properties of MgB$_2$ thin films. MgB$_2$ films of two thicknesses viz. 400 nm (MB400nm) and 800 nm (MB800nm) were irradiated by 350 keV C ions having a…
Superconducting thin films of MgB2 were deposited by Pulsed Laser Deposition on magnesium oxide and sapphire substrates. Samples grown at 450C in an argon buffer pressure of about 10-2 mbar by using a magnesium enriched target resulted to…
We studied the influence of sample preparation and defects in the superconducting properties samples using atomic ratios of Mg:B=1:1 and Mg:B=1:2. Samples were characterized by SEM, and XRD, and the magnetization properties were examined in…
We study the effects of pressure on the electron-phonon interaction in MgB_2 using density-functional-based methods. Our results show that the superconductivity in MgB_2 vanishes by 100 GPa, and then reappears at higher pressures. In…
Here, we report the discovery of superconductivity in a new transition metal-chalcogenide compound, i.e. Nb2Pd0.81S5, with a transition temperature Tc > 6.6 K. Despite its relatively low Tc, it displays remarkably high and anisotropic…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
Powdered and sintered MgB2 samples have been characterized through magnetic measurements performed from T = 5 K up to few degrees above the transition temperature of about 39 K. We found that the sintered samples behave as well-connected…
Over the past 14 years MgB2 has gone from a startling discovery to a promising, applied superconductor. In this article we present a brief overview of the synthesis and the basic superconducting properties of this remarkable compound. In…
Effects of magnetic impurity on the superconductivity has been investigated in Mg1-xMnB2. With increase of Mn concentration x, the lattice constant c (perpendicular to the boron sheet) decreases at a rate of -1.4 % (= dlnc/dx), while a…
The hydrostatic pressure effect on the newly discovered superconductor MgB2 has been determined. The transition temperature Tc was found to decrease linearly at a large rate of -1.6 K/GPa, in good quantitative agreement with the ensuing…
The dependence of Tc for MgB2 on purely hydrostatic or nearly hydrostatic pressure has been determined to 23 GPa for single-crystalline and to 32 GPa for polycrystalline samples, and found to be in good agreement. Tc decreases from 39 K at…
Measurements of the superconducting transition temperature Tc have been performed by the inductive method on MgB2 at pressures up to 28 GPa. Tc decreases with applied pressure, exhibiting a cusp at about 9 GPa. We interpret the appearance…
The effects of high-temperature vacuum-annealing induced Mg deficiency in MgB2 single crystals grown under high pressure were investigated. As the annealing temperature was increased from 800 to 975 C, the average Mg content in the MgB2…
MgB2 superconducting wires with critical temperature Tc approaching 40 K were used for preparation of MgB2/Ag and MgB2/In junctions. The differential conductance vs. voltage characteristics of N-S junctions exhibit clear contribution of…
We report on syntheses and electron transport properties of polycrystalline samples of diborides (AB2) with different transition metals atoms (A=Zr,Nb,Ta). The temperature dependence of resistivity, \rho(T), and ac susceptibility of these…
We report synthesis, structural details and complete superconducting characterization of very recently discovered Nb2PdS5 new superconductor. The synthesized compound is crystallized in mono-clinic structure. Bulk superconductivity is seen…