We report measurements on single crystals of orthorhombic CeNiGe2, which is found to exhibit highly anisotropic magnetic and transport properties. The magnetization ratio M(H//b)/M(H^b) at 2 K is observed to be about 18 at 4 T and the…
Anisotropic magnetic properties of single crystalline RAu_{2}Ge_{2} (R = La, Ce and Pr) compounds are reported. LaAu_{2}Ge_{2} exhibit a Pauli-paramagnetic behavior whereas CeAu_{2}Ge_{2} and PrAu_{2}Ge_{2} show an antiferromagnetic…
Ferromagnetic compound PrRu2Si2 exhibits a giant magnetocrystalline anisotropy of about 400 T. Its ordered moment below Tc=14K reaches 2.7 mB and is parallel to [0 0 1] crystalline direction. We have attributed the magnetism of PrRu2S2 to…
An antiferromagnetic transition is observed in single crystal EuRh2As2 at a high temperature T_N = 47 K compared to the ferromagnetic Weiss temperature theta = 12 K. We show that this is, surprisingly, consistent with mean field theory. A…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
Single crystal of PrSi was grown by Czochralski method in a tetra-arc furnace. Powder x-ray diffraction of the as grown crystal revealed that PrSi crystallizes in FeB$-$type structure with space group $Pnma$ (no. 62). PrSi undergoes a…
We report the results of ac and dc magnetic susceptibility (chi) and electrical resistivity (rho) measurements on the single crystals of Er2PdSi3, crystallizing in an AlB2-derived hexagonal structure, for two orientations H//[0001] and…
(Mn,Fe)2(P,Si) single crystals have been successfully grown by flux method. Single crystal diffraction demonstrates that Mn0.83Fe1.17P0.72Si0.28 crystallizes in a hexagonal crystal structure (space group P-62m) at both 100 and 280 K, in the…
Single crystals of BaFe$_2$As$_2$ and (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ have been grown out of excess Sn with 1% or less incorporation of solvent. The crystals are exceptionally micaceous, are easily exfoliated and can have dimensions as…
Single crystals of $R$Rh$_6$Ge$_4$ ($R$ = Pr, Nd, Sm, Gd - Er) were synthesized using a Bi flux and their physical properties were characterized by magnetization, resistivity, and specific heat measurements. These compounds crystallize in…
We report an optimized chemical vapor transport method to grow single crystals of (Mn$_{1-x}$Ni$_x$)$_2$P$_2$S$_6$ where x = 0, 0.3, 0.5, 0.7 & 1. Single crystals up to 4\,mm\,$\times$\,3\,mm\,$\times$\,200\,$\mu$m were obtained by this…
We report measurements of the temperature-dependent anisotropic resistivity and in-plane magnetoresistance on single crystals of the tetragonal heavy-fermion antiferromagnet (TN = 3.8 K) CeRhIn5. The measurements are reported in the…
Electrical resistivity rho, magnetic susceptibility chi, magnetization M and specific heat measurements are reported on a singlecrystalline sample of CePd5Al2, showing successive antiferromagnetic orderings at T_N1=4.1 K and T_N2=2.9 K. The…
We report anisotropic resistivity measurements of the heavy-fermion superconductor CeRh$_2$As$_2$ in magnetic fields up to 16 T and temperatures down to 0.35 K. The measured CeRh$_2$As$_2$ resistivity shows a signature corresponding to the…
We report the single crystal growth and anisotropic magnetic properties of the tetragonal RAg$_2$Ge$_2$ (R = Pr, Nd and Sm) compounds which crystallize in the ThCr$_2$Si$_2$ type crystal structure with the space group \textit{I4/mmm}. The…
Highly anisotropic properties of CeIr$_3$Si$_2$ have been observed by the magnetization $M$($B$), electrical resistivity $\rho$, and specific heat measurements on a single-crystalline sample. This compound with an orthorhombic structure…
We investigated magnetic, magnetotransport and magnetostriction properties of the A-type antiferromagnet Pr$_{0.46}$Sr$_{0.54}$MnO$_3$ which undergoes a first order paramagnetic-antiferromagnetic transition below T$_N$ = 210 K while cooling…
Electrical resistivity ($\rho$), magnetoresistance (MR), magnetization, thermopower and Hall effect measurements on the single crystal Gd$_{2}$PdSi$_3$, crystallizing in an AlB$_2$-derived hexagonal structure are reported. The well-defined…
The equiatomic PrGe single crystal was grown by Czochralski pulling method. The grown single crystal was found to have CrB-type orthorhombic crystal structure with the space group \textit{Cmcm} (#63). Transport and magnetization data reveal…
We report a study of anisotropy in transport and magnetic properties of K0.64Fe1.44Se2.00 single crystals. The anisotropy in resistivity is up to one order of magnitude between 1.8 K and 300 K. Magnetic susceptibility exhibits weak…