Superconductivity of high critical temperature ($T_{c}$) superconductors is usually realized through chemical dopant or application of pressure in a similar way to induce charge carriers of either electrons or holes into their parent…
We report the observation of a superconducting state below 8K coexistent with a spin-glass state caused by atomic disorder in Ce substituted Ca3Rh4Sn13. Measurements of specific heat, resistivity, and magnetism reveal the existence of…
We report suppression of superconductivity in Bi4O4S3 compound by Se doping at S site. Bulk polycrystalline samples are synthesized by solid state reaction route. The Rietveld refined of XRD data of all the studied samples show that the…
Application of pressures or electron-doping through Co substitution into Fe sites transforms the itinerant antiferromagnet BaFe(2)As(2) into a superconductor with the Tc exceeding 20K. We carried out systematic transport measurements of…
By partially substituting the tri-valence element La with di-valence element Sr in $LaOFeAs$, we introduced holes into the system. For the first time, we successfully synthesized the hole doped new superconductors $(La_{1-x}Sr_x)OFeAs$. The…
A systematic investigation has been performed by synthesis and comprehensive characterization of a series of SmFe1-xCuxAsO0.8F0.2 bulks (x = 0 to 0.2). These samples are well characterized by structural, Raman spectroscopy, microstructural,…
Superconductivity has been observed in doped SrTiO$_3$ at charge-carrier densities below 10$^{18}$ cm$^{-3}$, where the density of states at the Fermi level of the itinerant electrons is several orders of magnitude lower than that of…
In this study, we determined the effect of doping with the noble metal Ag on Ir$_2$Te$_4$ superconductors. Based on the resistivity, magnetization, and heat capacity, we explored the changes in the superconductivity and charge density wave…
Two different ferroelectric materials, Sr$_{0.95}$Ba$_{0.05}$TiO$_3$ and Sr$_{0.985}$Ca$_{0.015}$TiO$_3$, can be turned into polar metals with broken centrosymmetry via electron doping. Systematic substitution of Nb$^{5+}$ for Ti$^{4+}$ has…
We report an NMR investigation of the superconductivity in BaFe(2)As(2) induced by Co doping (Tc=22K). We demonstrate that Co atoms form an alloy with Fe atoms and donate carriers without creating localized moments. Our finding strongly…
We report the realization of superconductivity by an isovalent doping with phosphorus in LaFeAsO. X-ray diffraction shows that, with the partial substitution of P for As, the Fe$_2$As$_2$ layers are squeezed while the La$_2$O$_2$ layers are…
Characteristic normal-state charge transport is found in the oxygen-deficient iron-arsenides LnFeAsO1-y (Ln: La and Nd) with the highest Tc's among known Fe-based superconductors. The effect of "doping" in this system is mainly on the…
Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1-xKxFe2As2, which is the maximum found thus far among the 122 phases.…
Through the combination of X-ray diffraction, electrical transport, magnetic susceptibility, and the heat capacity measurements, we studied the effect of Ce doping in the newly discovered SrFBiS${2}$ system. It is found that…
In the iron-based high-Tc bulk superconductors, Tc above 50K was only observed in the electron-doped 1111-type compounds. Here we revisit the electron-doped SmFeAsO polycrystals to make a further investigation for the highest T-c in these…
It is demonstrated that SC mechanism of doped Fe-based compounds is characteristic for itinerant electron systems with coexistence of both (e-e)- and (e-h)-pairing arising due to electron-phonon and Coulomb interactions, respectively. The…
Dependence of superconducting properties of (Ca,RE)(Fe,TM)As2 [(Ca,RE)112, TM: Co, Ni)] on RE elements (RE = La-Gd) was systematically investigated. Improvement of superconducting properties by Co or Ni co-doping was observed for all…
Polycrystalline samples with nominal composition of Ba(Fe1-xIrx)2As2 (x=0.10, 0.15, and 0.20) were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), electrical resistivity, and magnetization measurements.…
It has been considered that FeAs-based high transition temperature (high-Tc) superconductors need electron or hole doping by aliovalent ion substitution or large off-stoichiometry in order to induce superconductivity. We report that…
We report the effect of 3d metal Cobalt (Co) and Nickel (Ni) doping on the FeTe0.5Se0.5 superconductor with the nominal composition range Fe1-xMxTe0.5Se0.5 (M = Co, Ni and x = 0.00, 0.01 0.02, 0.05, and 0.10). Samples are synthesized…