By substituting Fe with the 5d-transition metal Pt in BaFe2As2, we have successfully synthesized the superconductors BaFe2-xPtxAs2. The systematic evolution of the lattice constants indicates that the Fe ions were successfully replaced by…
In this paper we report the synthesis of iron-based superconductors CaFe2-xRhxAs2 using one-step solid state reaction method, which crystallizes in the ThCr2Si2-type structure with a space group I4/mmm. The systematic evolution of the…
Using one-step solid state reaction method, we have successfully synthesized the superconductor SrFe1-xRuxAs. X-ray diffraction indicates that the material has formed the ThCr2Si2-type structure with a space group I4/mmm. The systematic…
By substituting the Fe with the 4d and 5d-transition metals Rh, Ir and Pd in SrFe_2As_2, we have successfully synthesized a series of superconductors SrFe_{2-x}M_xAs_2 (M = Rh, Ir and Pd) and explored the phase diagrams of them. The…
By doping Rh to the Fe sites in SrFe2As2, superconductivity is induced when the antiferromagnetic (AF) order is suppressed. The maximum superconducting transition temperature was found at about 22 K with the doping level of x = 0.25. It is…
The recently discovered FeAs-based superconductors are a new, promising set of materials for both technological as well as basic research. They offer transition temperatures as high as 55 K as well as essentially isotropic and extremely…
We report the realization of superconductivity by 5d element Ir doping in LaFeAsO, a prototype parent compound of high-temperature iron based superconductors. X-ray diffraction patterns indicate that the material has formed the…
We have synthesized polycrystalline samples of Pt-substituted SrFe2As2 and measured the temperature dependence of magnetization and electrical resistivity. We have observed the superconducting transition at Tc = 17 K with the maximum…
By substituting the Fe with the 5d-transition metal Ir in SrFe2As2, we have successfully synthesized the superconductor SrFe2-xIrxAs2 with Tc = 22.3 K at x = 0.5. X-ray diffraction indicates that the material has formed the ThCr2Si2-type…
By using solid state reaction method we have fabricated the hole doped $La_{1-x}Sr_xFeAsO$ superconductors with Sr content up to 0.13. It is found that the sharp anomaly at about 150 K and the low temperature upturn of resistivity are…
Single crystals of the Ni-doped FeAs-based superconductor SrFe2-xNixAs2 were grown using a self-flux solution method and characterized via x-ray measurements and low temperature transport, magnetization, and specific heat studies. A doping…
We report the interplay between charge-density-wave (CDW) and superconductivity of 1$T$-Fe$_{x}$Ta$_{1-x}$S$_{2}$ ($0\leq x \leq 0.05$) single crystals. The CDW order is gradually suppressed by Fe-doping, accompanied by the disappearance of…
In iron pnictides, high temperature superconductivity emerges after suppressing antiferromagnetism by doping. Here we show that antiferromagnetism in Ca$_{1-x}$La$_x$FeAs$_2$ is robust against and even enhanced by doping. Using…
We have studied EuFe$_{2}$(As$_{0.7}$P$_{0.3}$)$_{2}$ by the measurements of x-ray diffraction, electrical resistivity, thermopower, magnetic susceptibility, magnetoresistance and specific heat. Partial substitution of As with P results in…
Electrical resistivity under high pressure have been measured on nominally pure SrFe2As2 up to 14 GPa. The resistivity drop appeared with increasing pressure, and we clearly observed zero resistivity. The maximum of superconducting…
The effects of simultaneous Sb doping on the superconductivity of 112-type Ca1-xRExFeAs2 (RE = La, Ce, Pr, and Nd) were studied through measurements of the magnetization and electrical resistivity. In Sb-free materials, the superconducting…
We report the synthesis and characterization of antimony doped oxypnictide superconductor, LaO0.8F0.2FeAs1-xSbx (x = 0.05 and 0.10). The parent compound LaOFeAs with fluorine doping exhibits superconductivity at maximum transition…
Superconductivity with zero resistance transition temperature (Tc) up to 8.4 K and 8.3 K can be obtained by doping cobalt and sodium in alfa-FeSe with the nominal composition of Fe0.92Co0.08Se and Na0.1FeSe, respectively. The electrical…
Single crystals of SrFe2-xPtxAs2 (0 < x < 0.36) were grown using the self flux solution method and characterized using x-ray crystallography, electrical transport, magnetic susceptibility, and specific heat measurements. The…
Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1-xKxFe2As2, which is the maximum found thus far among the 122 phases.…