Related papers: Superconductivity at 22.3 K in SrFe2-xIrxAs2
We have synthesized polycrystalline samples of Pt-substituted SrFe2As2 and measured the temperature dependence of magnetization and electrical resistivity. We have observed the superconducting transition at Tc = 17 K with the maximum…
Using one-step solid state reaction method, we have successfully synthesized the superconductor SrFe1-xRuxAs. X-ray diffraction indicates that the material has formed the ThCr2Si2-type structure with a space group I4/mmm. The systematic…
In the electron doped compounds SrFe_(2-x)Co_xAs_2 superconductivity with T_c up to 20 K is observed for 0.2 < x < 0.4. Results of structure determination, magnetic susceptibility, electrical resistivity, and specific heat are reported. The…
In this paper we report the synthesis of iron-based superconductors CaFe2-xRhxAs2 using one-step solid state reaction method, which crystallizes in the ThCr2Si2-type structure with a space group I4/mmm. The systematic evolution of the…
Compounds of Sr1-xLaxFe2As2 were synthesized by solid state reaction at 1273 K, under pressures of 2 or 3 GPa. The Sr1-xLaxFe2As2 phase was dominant up to x = 0.5, and superconductivity was observed at $x \ge 0.2$. A maximum critical…
Superconductivity was achieved in Ti-doped iron-arsenide compound Sr4Cr0.8Ti1.2O6Fe2As2 (abbreviated as Cr-FeAs-42622). The x-ray diffraction measurement shows that this material has a layered structure with the space group of…
We report the realization of superconductivity by 5d element Ir doping in LaFeAsO, a prototype parent compound of high-temperature iron based superconductors. X-ray diffraction patterns indicate that the material has formed the…
Electrical resistivity under high pressure have been measured on nominally pure SrFe2As2 up to 14 GPa. The resistivity drop appeared with increasing pressure, and we clearly observed zero resistivity. The maximum of superconducting…
By using solid state reaction method, we have synthesized the Pd-doped superconductor SrFe2-xPdxAs2. The systematic evolution of the lattice constants indicated that the Fe ions were successfully replaced by the Pd. By increasing the doping…
Polycrystalline samples with nominal composition of Ba(Fe1-xIrx)2As2 (x=0.10, 0.15, and 0.20) were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), electrical resistivity, and magnetization measurements.…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…
BaFe2As2 is the parent compound of the '122' iron arsenide superconductors and crystallizes with the tetragonal ThCr2Si2 type structure, space group I4/mmm. A spin density wave transition at 140 K is accompanied by a symmetry reduction to…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
The superconductor Sr4V2O6Fe2As2 with transition temperature at 37.2 K has been fabricated. It has a layered structure with the space group of p4/nmm, and with the lattice constants a = 3.9296Aand c = 15.6732A. The observed large…
By doping Rh to the Fe sites in SrFe2As2, superconductivity is induced when the antiferromagnetic (AF) order is suppressed. The maximum superconducting transition temperature was found at about 22 K with the doping level of x = 0.25. It is…
A series of layered (Sr$_{1-x}$K$_x$)Fe$_2$As$_2$ compounds with nominal x=0 to 0.40 are synthesized by solid state reaction method. Similar to other parent compounds of iron-based pnictide superconductors, the pure SrFe$_2$As$_2$ shows a…
The magnetism in SrFe2As2 can be suppressed by electron doping through a small substitution of Fe by Co or Ni, giving way to superconductivity. We demonstrate that a massive substitution of Fe by isovalent ruthenium similarly suppresses the…
By substituting the Fe with the 4d and 5d-transition metals Rh, Ir and Pd in SrFe_2As_2, we have successfully synthesized a series of superconductors SrFe_{2-x}M_xAs_2 (M = Rh, Ir and Pd) and explored the phase diagrams of them. The…
Measurements of the Hall effect, thermoelectric power, magnetic susceptibility and upper and lower critical fields were performed on single crystals of SrFe(2-x)Ni(x)As2, an FeAs-based superconducting system that exhibits a reduced…
By substituting Fe with the 5d-transition metal Pt in BaFe2As2, we have successfully synthesized the superconductors BaFe2-xPtxAs2. The systematic evolution of the lattice constants indicates that the Fe ions were successfully replaced by…