Single crystals of A$_{1-x}$K$_x$Fe$_2$As$_2$ (A=Ba, Sr) with high quality have been grown successfully by FeAs self-flux method. The samples have sizes up to 4 mm with flat and shiny surfaces. The X-ray diffraction patterns suggest that…
Centimeter sized platelet single crystals of KFe2As2 were grown using a self-flux method. An encapsulation technique using commercial stainless steel container allowed the stable crystal growth lasting for more than 2 weeks. Ternary K-Fe-As…
We measured resistivity and specific heat of high-quality CsFe$_2$As$_2$ single crystals, which were grown by using a self-flux method. The CsFe$_2$As$_2$ crystal shows sharp superconducting transition at 1.8 K with the transition width of…
We report the single crystal growth of Ca(Fe1-xCox)2As2 (0 <= x <= 0.082) from Sn flux. The temperature-composition phase diagram is mapped out based on the magnetic susceptibility and electrical transport measurements. Phase diagram of…
We report the successful growth of high quality single crystals of LiFeAs with lateral sizes up to 5 x 5 mm2 by the Sn-flux method. Electrical resistivity studies reveal that the superconducting onset temperature is 18.2 K with a transition…
Single crystals of Ba0.6K0.4Fe2As2 with excellent quality have been successfully grown without fluxing agent through a simple one-step method for the first time. X-ray diffraction patterns demonstrate that the samples have high crystalline…
Single crystals of K$_x$Fe$_{2-y}$Se$_2$ are prepared by quenching at various temperatures. The crystals obtained at higher quenching temperatures have a surface morphology with mesh-like texture. They show a sharp superconducting…
Millimeter sized single crystals of CaFe$_{1-x}$Co$_x$AsF were grown using a self-flux method. It is found that high-quality single crystals can be grown from three approaches with different initial raw materials. The chemical compositions…
Single crystals of BaFe$_2$As$_2$ and (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ have been grown out of excess Sn with 1% or less incorporation of solvent. The crystals are exceptionally micaceous, are easily exfoliated and can have dimensions as…
Superconducting single crystals of SmFeAsO$_{1-x}$ without fluorine doping were grown at a pressure of 3.3 GPa and a temperature of 1350-1450 $^\circ$C by using the self-flux method. Plate-like single crystals of a few-150 $\mu$m in their…
Superconductivity has been explored in single crystals of the Ni-doped FeAs-compound SrFe2-xNixAs2 grown by self-flux solution method. The antiferromagnetic order associated with the magnetostructural transition of the parent compound…
Single crystals of undoped CaFe2As2 were grown by a FeAs self-flux method, and the crystals were quenched in ice-water rapidly after high temperature growth. The quenched crystal undergoes a collapsed tetragonal structural phase transition…
Single crystals of SrFe2-xPtxAs2 (0 < x < 0.36) were grown using the self flux solution method and characterized using x-ray crystallography, electrical transport, magnetic susceptibility, and specific heat measurements. The…
Large high-quality single crystals of hole-doped iron-based superconductor (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$ were grown over a broad composition range $0.22 \leq x \leq 1$ by inverted temperature gradient method. We found that high soaking…
We report a simple, reliable method to grow high quality BaFe$_{2-x}$Co$_x$As$_2$ single crystal samples without using any fluxing agent. The starting materials for the single crystal growth come from well-crystallized polycrystalline…
We have attempted the crystal growth by the traveling-solvent floating-zone (TSFZ) method of La_{2-x}Ba_xCuO_4 with x~1/8, where the superconductivity is strongly suppressed. Under flowing O_2-gas of a high pressure (4 bars), we have…
We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting…
SrPt$_2$As$_2$ single crystals with CaBe$_2$Ge$_2$-type structure were synthesized by self-melting technique. X-ray diffraction, transmission electron microscopy, electrical resistivity, specific heat and optical spectroscopy measurements…
We investigated the occurrence and nature of superconductivity in single crystals of YFe$_2$Ge$_2$ grown out of Sn flux by employing x-ray diffraction, electrical resistivity, and specific heat measurements. We found that the residual…
Single crystals of mixed alkaline earth metal iron arsenide materials of Ba1-xSrxFe2As2 and Ba0.5Sr0.5(Fe1-yCoy)2As2 are synthesized via the self-flux method. Ba1-xSrxFe2As2 display spin-density wave features (TN) at temperatures…