The dynamic fragmentation of residually stressed solids involves a complex interplay between stored elastic energy, stress wave propagation, and crack instabilities. In this work, we investigate the fracture mechanics of chemically…
Understanding, predicting and eventually improving the resistance to fracture of silicate materials is of primary importance to design new glasses that would be tougher, while retaining their transparency. However, the atomic mechanism of…
We report here atomic force microscopy experiments designed to uncover the nature of failure mechanisms occuring within the process zone at the tip of a crack propagating into a silica glass specimen under stress corrosion. The crack…
The purpose of this paper is to fill the gap between the classical treatment of brittle fracture mechanics and the new idea of considering the crack evolution as a free discontinuity problem. Griffith and Irwin criterions of crack…
The process of frictional rupture, i.e. the failure of frictional systems, abounds in the technological and natural world around us, ranging from squealing car brake pads to earthquakes along geological faults. A general framework for…
We employ a recently developed model that allows the study of two-dimensional brittle crack propagation under fixed grip boundary conditions. The crack development highlights the importance of voids which appear ahead of the crack as…
Long-term corrosion of glass is studied using polarising light microscopy, FTIR and SEM including EDX and elemental mapping. Early 19th century beads made of lead-potassium glass are the object of the study. Non-uniformly distributed…
Unstable growth of cracks (rough crack surface and crack branching) in dynamic fracture has long been observed in various materials. Until now, there was no universally agreed upon explanation for these instabilities. Here, we demonstrate…
Glass is highly sensitive to surface flaws generated by contact. Surface cracks threaten both its mechanical strength and visual aspect. Recent trends in glass functionalisation by grafting or coating lend an even more prominent role to the…
We use large-scale simulations to investigate the dynamic fracture of silica and sodium-silicate glasses under uniaxial tension. The stress-strain curves demonstrate that silica glass is brittle whereas the glasses rich in Na show…
We report in situ Atomic Force Microscopy experiments which reveal the presence of nanoscale damage cavities ahead of a stress-corrosion crack tip in glass. Their presence might explain the departure from linear elasticity observed in the…
Shear bands lie at the root of fracture initiation in bulk metallic glasses and amorphous polymers. For silicate glasses, in contrast, studies have largely emphasized permanent volumetric strain, commonly referred to as densification. Here…
Crack propagation is studied in a two dimensional decagonal model quasicrystal. The simulations reveal the dominating role of highly coordinated atomic environments as structure intrinsic obstacles for both dislocation motion and crack…
Stress corrosion cracking (SCC) is a form of failure in metals that is present mostly in systems where humidity contact and mechanical load play a key role. Therefore, prediction of the combined effect is desired. There are models based on…
The fracture energy of brittle materials rises with crack velocity, and this effect is typically attributed to surface roughening from path instabilities. Here we show, using molecular dynamics simulations of silica glass with a…
An original setup combining a very stable loading stage, an atomic force microscope and an environmental chamber, allows to obtain very stable sub-critical fracture propagation in oxide glasses under controlled environment, and subsequently…
Crack growth is the basic mechanism leading to the failure of brittle materials. Engineering addresses this problem within the framework of continuum mechanics, which links deterministically the crack motion to the applied loading. Such an…
I study the influence of temperature and the crack-tip velocity of the bond breaking at the crack tip in rubber-like materials. The bond breaking is considered as a stress-aided thermally activated process and result in an effective crack…
These notes address the mechanics of propagating hydraulic fractures (HF). In the first part, we focus on how different physical mechanisms (dissipation in fluid and solid, fluid storage in fracture and its exchange with permeable rock,…
Ever since the very first human-made knapped tools, the control of fracture propagation in brittle materials has been a vector of technological development. Nowadays, a broad range of applications relies on crack propagation control, from…