Related papers: Connectivity and Critical Currents in Polycrystall…
We synthesized polycrystalline MgB2 from a stoichiometric mixture of Mg and the 11 B isotope under different conditions. All the samples showed bulk superconductivity with Tc = 38~39 K. The samples containing the least amount of unreacted…
High quality bulk MgB2 exhibit a structure of voids and agglomeration of crystals on different length-scales. Because of this, the superconducting currents percolate between the voids in the ensuing structure. Magnetic measurements reveal…
In this contribution, different concepts for mechanically reinforced MgB2 wires with high transport currents are presented and characterised. It is shown that the achieved critical transport currents depend strongly on the conductor…
Magnesium diboride (MgB2) powder was mechanically alloyed by high energy ball milling with C to a composition of Mg(B0.95C0.05)2 and then sintered at 1000 C in a hot isostatic press. Milling times varied from 1 minute to 3000 minutes. Full…
Ex-situ Powder-In-Tube MgB2 tapes prepared with ball-milled, undoped powders showed a strong enhancement of the irreversibility field H*, the upper critical field Hc2 and the critical current density Jc(H) together with the suppression of…
Magnetotransport measurements are presented on polycrystalline MgB2 samples. The resistive upper critical magnetic field reveals a temperature dependence with a positive curvature from Tc = 39.3 K down to about 20 K, then changes to a…
The transport of electrical current through a superconductor falls into three broad regimes: non-dissipative, dissipative but superconducting, and normal or non-superconducting. These regimes are demarkated by two definitions of critical…
Bulk samples of MgB2 were prepared with 5, 10, and 15% wt.% Y2O3 nanoparticles added using a simple solid-state reaction route. Transmission electron microscopy (TEM) showed a fine nanostructure consisting of ~3-5 nm YB4 nanoparticles…
Here we describe the results of an atomic resolution study of the structure and composition of both the interior of the grains, and the grain boundaries in polycrystalline MgB2. We find that there is no oxygen within the bulk of the grains…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
We demonstrate direct evidence of possible surface superconductivity on small, well-shaped MgB2 single crystals. Transport measurements in the range H < 1.6 Hc2^c, where Hc2^c is the bulk upper critical field for the c axis, show non-Ohmic…
We report dc transport and magnetization measurements of Jc in MgB2 wires fabricated by the powder-in-tube method, using commercial MgB2 powder with 5 %at Mg powder added as an additional source of magnesium, and stainless steel as sheath…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
The influence of the oxygen segregation into Mg-B-O inclusions (which are oxygen enriched as compared to the matrix material) and the formation of boron enriched phases (with near MgB12 composition) in MgB2 structure on pinning in magnesium…
Despite the intense activity in the year since the discovery of superconductivity in MgB2, key parameters, in particular the upper and lower critical fields Hc2 and Hc1 and their anisotropies, are not well-established, largely because of…
The recently discovered superconductivity in MgB2 has captured world attention due to its simple crystal structure and relatively high superconducting transition temperature Tc=39K. It appears to be generally accepted that it is…
We report a detailed study of the microstructure and defects in sintered polycrystalline MgB2. Both TEM and x-ray data reveal that MgO is the major second-phase in our bulk samples. Although MgB2 and MgO have different crystal symmetries,…
We have conducted pulsed transport measurements on c-axis oriented magnesium diboride films over the entire relevant ranges of magnetic field $0 \alt H \alt H_{c2}$ (where \hcu is the upper critical field) and current density $0 \alt j \alt…
We report on tunneling and Andreev-reflection conductance spectra of 39 K superconducting magnesium diboride, obtained with Pb and Au counter-electrodes. Two distinct steps at close to 2.7 and 7.1 meV appear in a low-resistance…
The pair-breaking critical current density j_{d} of magnesium diboride was determined over its entire temperature range by a pulsed dc transport measurement. At fixed low values of current density j, the resistive transition temperature Tc…