Related papers: Superconductivity at 56 K in Samarium-doped SrFeAs…
Since the discovery of superconductivity\cite{1} at 26 K in oxy-pnictide $LaFeAsO_{1-x}F_x$, enormous interests have been stimulated in the fields of condensed matter physics and material sciences. Among the five different structures in…
Here we report the superconductivity in the iron-based oxyarsenide Sm[O1-xFx]FeAs, with the onset resistivity transition temperature at 55.0 K and Meissner transition at 54.6 K. This compound has the same crystal structure as LaOFeAs with…
The recently discovered quaternary arsenide oxide superconductor La[O1-xFx]FeAs with the superconducting critical transition temperature (Tc) of 26 K [1], has been quickly expanded to another high-Tc superconducting system beyond copper…
The Phase diagram of SmFeAsO1-xFx in terms of x is exhibited in this study. SmFeAsO1-xFx from x = 0 to x = 0.3 were prepared by low temperature sintering with slow cooling. The low temperature sintering suppresses the formation of the…
Here we report the fabrication and superconductivity of the iron-based arsenic-oxide GdFeAsO1-delta compound with oxygen-deficiency, which has an onset resistivity transition temperature at 53.5 K. This material has a same crystal structure…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
Superconductivity was achieved in Ti-doped iron-arsenide compound Sr4Cr0.8Ti1.2O6Fe2As2 (abbreviated as Cr-FeAs-42622). The x-ray diffraction measurement shows that this material has a layered structure with the space group of…
By substituting the Fe with the 5d-transition metal Ir in SrFe2As2, we have successfully synthesized the superconductor SrFe2-xIrxAs2 with Tc = 22.3 K at x = 0.5. X-ray diffraction indicates that the material has formed the ThCr2Si2-type…
We have synthesized a quaternary fluoroarsenide SrFeAsF with the ZrCuSiAs-type structure (P4/nmm, a = 0.3999 and c = 0.8973 nm), which is composed of an alternately stacked (FeAs)- and (SrF)+ layers, analogous to the FeAs-based…
We have successfully synthesized the fluoride-arsenide compounds Ca$_{1-x}$RE$_x$FeAsF (RE=Nd, Pr; x=0, 0.6). The x-ray powder diffraction confirmed that the main phases of our samples are Ca$_{1-x}$RE$_x$FeAsF with the ZrCuSiAs structure.…
Since the discovery of copper oxide superconductor in 1986 [1], extensive efforts have been devoted to the search of new high-Tc superconducting materials, especially high-Tc systems other than cuprates. The recently discovered quaternary…
Since the discovery of high-transition temperature ($T_c$) superconductivity in layered copper oxides, extensive efforts have been devoted to explore the higher $T_c$ superconductivity. However, the $T_c$ higher than 40 K can be obtained…
Pure phases of a new oxyarsenide superconductor of the nominal composition CeOFe0.9Co0.1As was successfully synthesized by solid state reaction in sealed silica ampoules at 1180 C. It crystallizes in the layered tetragonal ZrCuSiAs type…
Superconductivity with Tc of 45 K was realized in the tetragonal ZrCuSiAs-type PrOxFeAs (x=0.75) under heat treatment of 1300 oC and pressure of 6 GPa for 2 hours. Although the sample prepared at 900 oC in vaccum possessed the same phase as…
Using one-step solid state reaction method, we have successfully synthesized the superconductor SrFe1-xRuxAs. X-ray diffraction indicates that the material has formed the ThCr2Si2-type structure with a space group I4/mmm. The systematic…
A series of layered (Sr$_{1-x}$K$_x$)Fe$_2$As$_2$ compounds with nominal x=0 to 0.40 are synthesized by solid state reaction method. Similar to other parent compounds of iron-based pnictide superconductors, the pure SrFe$_2$As$_2$ shows a…
Aliovalent rare earth substitution into the alkaline earth site of CaFe2As2 single-crystals is used to fine-tune structural, magnetic and electronic properties of this iron-based superconducting system. Neutron and single crystal x-ray…
We report the discovery of superconductivity at high pressure in SrFe2As2 and BaFe2As2. The superconducting transition temperatures are up to 27 K in SrFe2As2 and 29 K in BaFe2As2, making these the highest pressure-induced superconducting…
Superconductivity with zero resistance transition temperature (Tc) up to 8.4 K and 8.3 K can be obtained by doping cobalt and sodium in alfa-FeSe with the nominal composition of Fe0.92Co0.08Se and Na0.1FeSe, respectively. The electrical…
Exploring new unconventional superconductors is of great value for both fundamental research and practical applications. It is a long-term challenge to develop and study more hole-doped superconductors in 1111 system of iron-based…