Related papers: Pressure-induced superconductivity in Iron pnictid…
We report bulk superconductivity induced by an isovalent doping of phosphorus in BaFe$_{2}$(As$_{1-x}$P$_{x}$)$_{2}$. The P-for-As substitution results in shrinkage of lattice, especially for the FeAs block layers. The resistivity anomaly…
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…
Superconductivity with Tc of 45 K was realized in the tetragonal ZrCuSiAs-type PrOxFeAs (x=0.75) under heat treatment of 1300 oC and pressure of 6 GPa for 2 hours. Although the sample prepared at 900 oC in vaccum possessed the same phase as…
The magnetism in SrFe2As2 can be suppressed by electron doping through a small substitution of Fe by Co or Ni, giving way to superconductivity. We demonstrate that a massive substitution of Fe by isovalent ruthenium similarly suppresses the…
Here we report the superconductivity in the LaFeAsO1-xFx system prepared by high pressure synthesis. The highest onset superconducting transition temperature (Tc) in this La-based system is 41.0 K with the nominal composition of…
It is demonstrated that resistive transition at 203 K observed in metallic sulfur hydride system at high pressure can be magnetic (rather than superconducting (SC)) in nature. The onset temperature of genuine superconducting transition in…
We have studied EuFe$_{2}$(As$_{0.7}$P$_{0.3}$)$_{2}$ by the measurements of x-ray diffraction, electrical resistivity, thermopower, magnetic susceptibility, magnetoresistance and specific heat. Partial substitution of As with P results in…
NdFeAsO0.88F0.12 belongs to the recently discovered family of high-TC iron-based superconductors. The influence of high pressure on transport properties of this material has been studied. Contrary to La-based compounds, we did not observe a…
Here we report pressure effect on superconducting transition temperature (Tc) of ReFeAsO0.85 (Re= Sm and Nd) system without fluorine doping. In-situ measurements under high pressure showed that Tc of the two compounds decrease monotonously…
Very recently, NiTe2 has been reported to be a type II Dirac semimetal with Dirac nodes near the Fermi surface. Furthermore, it is unveiled that NiTe2 presents the Hall Effect, which is ascribed to orbital magnetoresistance. The physical…
We report the precise pressure dependence of FeSe from a resistivity measurement up to 4.15 GPa. Superconducting transition temperature (T_c) increases sensitively under pressure, but shows a plateau between 0.5-1.5 GPa. The maximum T_c,…
We have successfully grown single crystalline NaFeAs with cobalt or phosphor doping. Bulk superconductivity occurs in NaFe$_{0.95}$Co$_{0.05}$As at 19 K while much higher transition temperature is observed in NaFeAs$_{0.8}$P$_{0.2}$, in…
The superconducting transition temperatures, $T_{\mathrm{c}}$, of La$_{4}$Ni$_{3}$O$_{10+\delta}$($\delta$ = 0.04 and -0.01) were determined under various pressures up to 124.9 GPa by electrical resistance measurements with a diamond anvil…
We report the ac magnetic susceptibility $\chi_{ac}$ and resistivity $\rho$ measurements of EuFe$_2$As$_2$ under high pressure $P$. By observing nearly 100% superconducting shielding and zero resistivity at $P$ = 28 kbar, we establish that…
Bulk superconductivity was discovered in BaRh2P2 (Tc = 1.0 K) and BaIr2P2 (Tc = 2.1 K), which are isostructural to (Ba,K)Fe2As2, indicative of the appearance of superconductivity over a wide variety of layered transition metal pnictides.…
Pressure dependence of superconducting transition temperature $T_{\rm c}$ has been determined through the DC magnetic measurements under pressure up to $P$=10 GPa for $\beta$-pyrochlore oxides AOs$_2$O$_6$ with A=Cs ($T_{\rm c}$=3.3 K), Rb…
Temperature-dependent in-plane, $\rho_a(T)$, and inter-plane, $\rho_c(T)$, resistivities were measured for the iron-arsenide superconductor (Ba$_{1-x}$K$_x$)Fe $_2$As$_2$ over a broad doping range from parent compound to optimal doping…
Measurements of the Hall effect, thermoelectric power, magnetic susceptibility and upper and lower critical fields were performed on single crystals of SrFe(2-x)Ni(x)As2, an FeAs-based superconducting system that exhibits a reduced…
Various tin hydrides SnHx (x = 4, 8, 12, 14) have been theoretically predicted to be stable at high pressures and to show high-critical-temperature superconductivity with Tc ranging from about 70 to 100 K. However, experimental…
The discovery of superconductivity of about 30 K in iron selenides with very large magnetic moments simulates the examination of completing orders. Here we report a finding of pressure- induced suppression of the superconducting transition…