Since the discovery of copper oxide superconductor in 1986 [1], extensive efforts have been devoted to the search of new high-Tc superconducting materials, especially high-Tc systems other than cuprates. The recently discovered quaternary…
We report $^{75}$As nuclear quadrupole resonance (NQR) studies on superconducting oxypnictide LaFeAsO$_{0.92}$F$_{0.08}$ ($T_{\rm c}$ = 23 K). The temperature dependence of the spin lattice relaxation rate (1/$T_1$) decreases below $T_{\rm…
The highest superconducting temperature T$_c$ observed in any elemental metal (Li with T$_c$ ~ 20 K at pressure P ~ 40 GPa) is shown to arise from critical (formally divergent) electron-phonon coupling to the transverse T$_1$ phonon branch…
The recently discovered quaternary arsenide oxide superconductor La[O1-xFx]FeAs with the superconducting critical transition temperature (Tc) of 26 K [1], has been quickly expanded to another high-Tc superconducting system beyond copper…
Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1-xKxFe2As2, which is the maximum found thus far among the 122 phases.…
The recent discovery of superconductivity with relatively high transition temperature Tc in the layered iron-based quaternary oxypnictides La[ O1-xFx] FeAs was a real surprise. The excitement generated can be seen by the number of…
We investigated pressure effects on transition temperature (Tc) of the new iron-based superconductor K0.8Fe2Se2 using a BeCu/NiCrAl hybrid-type clamped piston-cylinder cell. The Tc(onset) was 33K at 0.85 GPa. With increasing pressure,…
Layered \textit{Ln}OBiS$_2$ compounds with \textit{Ln} = La, Ce, Pr, Nd, and Yb can be rendered conducting and superconducting via two routes, substitution of F for O or the tetravalent ions Ti, Zr, Hf, and Th for trivalent \textit{Ln}…
High-pressure electrical resistivity measurements up to 3.0GPa have been performed on EuFe2As2 single crystals with residual resistivity ratios RRR=7 and 15. At ambient pressure, a magnetic / structural transition related to FeAs-layers is…
The pressure induced superconductivity and structural evolution for Bi2Se3 single crystal have been studied. The emergence of superconductivity with onset transition temperature (Tc) about 4.4K is observed around 12GPa. Tc increases rapidly…
We report that the incorporation of hydroxide ions (OH)- significantly enhances the superconducting transition temperature (Tc) in the LnFeAsO-based superconductors (Ln1111: Ln = La, Ce and Pr). For La1111, Tc of the (OH)- incorporated…
We report the synthesis and characterization of the novel silicide LaFeSiH displaying superconductivity with onset at 11 K. We find that this pnictogen-free compound is isostructural to LaFeAsO, with a similar low-temperature tetragonal to…
We have investigated uniaxial pressure effect on superconductivity of pure Sr2RuO4, whose intrinsic superconducting transition temperature Tc is 1.5 K. It was revealed that a very low uniaxial pressure along the c axis, only 0.2 GPa,…
We report the observation of superconductivity at 33 K in K-doped 1,2:8,9-dibenzopentacene (C30H18). This is higher than any Tc reported previously for an organic superconductor besides the alkali-metal doped C60. This finding provides an…
The interplay between different ordered phases, such as superconducting, charge or spin ordered phases, is of central interest in condensed matter physics. The very recent discovery of superconductivity with a remarkable T$_c$= 26 K in…
We have studied the structural and superconductivity properties of the compound LaFeAsO0.9F0.1 under pressures up to 32GPa using synchrotron radiation and diamond anvil cells. We obtain an ambient pressure bulk modulus K_0 = 78(2)GPa,…
We have synthesized a quaternary fluoroarsenide SrFeAsF with the ZrCuSiAs-type structure (P4/nmm, a = 0.3999 and c = 0.8973 nm), which is composed of an alternately stacked (FeAs)- and (SrF)+ layers, analogous to the FeAs-based…
Recently, an extremely high superconducting temperature (Tc) of ~200 K has been reported in the sulfur hydride system above 100 GPa. This result is supported by theoretical predictions and verified experimentally. The crystal structure of…
The magnetic and transport behaviors of cerium substituted iron oxy-arsenide superconductor with x = 0.1 to 0.4 fluoride (F) doping have been investigated in this report. Temperature dependent susceptibility and resistivity measurements…
We have discovered a new iron pnictide oxide superconductor (Fe2As2)(Sr4(Mg,Ti)2O6). This material is isostructual with (Fe2As2)(Sr4M2O6) (M = Sc, Cr), which was found in our previous study. The structure of this compound is tetragonal with…