Related papers: Superconductivity at 27 K in tetragonal FeSe under…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
We investigated the pressure effects on the FeSe superconductor and the related compounds. Pressure dependence of superconducting transition temperature (Tc) for FeSe0.8S0.2 exhibits a dome-shaped behavior below 0.76 GPa. On the other hand,…
In contrast to bulk FeSe superconductor, heavily electron-doped FeSe-derived superconductors show relatively high Tc without hole Fermi surfaces and nodal superconducting gap structure, which pose great challenges on pairing theories in the…
We report pressure-induced superconductivity in a single crystal of CaFe2As2. At atmospheric pressure, this material is antiferromagnetic below 170 K but under an applied pressure of 0.69 GPa becomes superconducting, with a transition…
We synthesized tetragonal alpha-FeSe by melting a powder mixture of iron and selenium at high pressure. Subsequent annealing at normal pressure results in removing traces of hexagonal beta- FeSe, formation of a rather sharp transition to…
New iron selenide superconductors by intercalating smaller-sized alkali metals (Li, Na) and alkaline earths using high-temperature routes have been pursued ever since the discovery of superconductivity at about 30 K in KFe2Se2, but all have…
The highest critical temperature of superconductivity Tc has been achieved in cuprates: 133 K at ambient pressure and 164 K at high pressures. As the nature of superconductivity in these materials is still not disclosed, the prospects for a…
To explore new superconductors beyond the copper-based and iron-based systems is very important. The Ru element locates just below the Fe in the periodic table and behaves like the Fe in many ways. One of the common thread to induce high…
We have performed several high-pressure resistivity experiments on the recently discovered superconductors La[O_{0.89}F_{0.11}]FeAs and Ce[O_{0.88}F_{0.12}]FeAs. At ambient pressure, these materials have superconducting onset temperatures…
Superconducting FeSe in the form of wires and tapes were successfully fabricated using a novel gas diffusion procedure. Structural analysis by mean of x-ray diffraction shows that themain phase of tetragonal PbO-type FeSe was obtained by…
Superconductivity with Tc of 45 K was realized in the tetragonal ZrCuSiAs-type PrOxFeAs (x=0.75) under heat treatment of 1300 oC and pressure of 6 GPa for 2 hours. Although the sample prepared at 900 oC in vaccum possessed the same phase as…
Superconductivity with zero resistance transition temperature (Tc) up to 8.4 K and 8.3 K can be obtained by doping cobalt and sodium in alfa-FeSe with the nominal composition of Fe0.92Co0.08Se and Na0.1FeSe, respectively. The electrical…
We report an enhancement of superconducting transition temperature ($T_{\rm c}$) when Chromium (Cr) is substituted in excess at the Iron (Fe) site (FeCr$_x$Se, $x=$0.01, 0.02 and 0.03). There is a corresponding increase in the…
Here, we report the synthesis and characterization of sulphur-substituted iron telluride i.e. FeTe1-xSx; (x = 0-30 %) system and study the impact of low temperature oxygen (O2) annealing as well. Rietveld analysis of room temperature x-ray…
High pressure electrical resistance and x-ray diffraction measurements have been performed on ruthenium-doped Ba(Fe0.9Ru0.1)2As2, up to pressures of 32 GPa and down to temperatures of 10 K, using designer diamond anvils under…
Recently, interface has been employed to enhance superconductivity in the single-layer FeSe films grown on SrTiO3(001)(STO) with a possible Tc of ~ 80 K, which is nearly ten times of the Tc of bulk FeSe and is above the Tc record of 56 K…
Unlike the parent phases of the iron-arsenide high Tc superconductors, undoped FeSe is not magnetically ordered and exhibits superconductivity with Tc~9K. Equally surprising is the fact that applied pressure dramatically enhances the modest…
We report here that a new superconducting phase with much higher Tc has been found in K intercalated FeSe compound with excess Fe. We successfully grew crystals by precisely controlling the starting amount of Fe. Besides the superconducting…
Stabilized FeSe thin films in ambient pressure with tunable superconductivity would be a promising candidate for superconducting electronic devices yet its superconducting transition temperature (Tc) is below 10 K in bulk materials. By…
Superconductivity of transition metal dichalcogenide $1T$-TiTe$_2$ under high pressure was investigated by the first-principles calculations. Our results show that the superconductivity of $1T$-TiTe$_2$ exhibits very different behavior…