Related papers: LiFeAs: An Intrinsic FeAs-based Superconductor wit…
High quality Rb0.8Fe1.6+xSe2 single crystals are grown by a one step melting growth method. Superconductivity has been observed in all samples with x more than 0.05 and the maximum critical temperature Tc~32 K has been obtained in samples…
By substituting the Fe with the 5d-transition metal Ir in SrFe2As2, we have successfully synthesized the superconductor SrFe2-xIrxAs2 with Tc = 22.3 K at x = 0.5. X-ray diffraction indicates that the material has formed the ThCr2Si2-type…
We have synthesized a quaternary fluoroarsenide SrFeAsF with the ZrCuSiAs-type structure (P4/nmm, a = 0.3999 and c = 0.8973 nm), which is composed of an alternately stacked (FeAs)- and (SrF)+ layers, analogous to the FeAs-based…
We report an easy and versatile one-step route of synthesis for newly discovered Fe based superconductor LaFeAsO1-d with d = 0.0 to 0.15. Instead of widely used high-pressure-high-temperature (HPHT) synthesis, we applied the normal…
Recently a new family of Cr-based A2Cr3As3 (A = K, Rb, Cs) superconductors were reported, which own a rare quasi-one-dimensional (Q1D) crystal structure with infinite (Cr3As3)2- chains and exhibit intriguing superconducting characteristics…
The temperature dependence of the ac susceptibility for single-crystalline Fe1.02Se has been measured at high pressures to 6.7 GPa. The superconducting transition temperature Tc displays a large increase from 7 K to 30 K in the two-phase…
Two single crystalline samples with the same nominal composition of Rb0.8Fe2Se2 prepared via slightly different precursor routes under the same thermal processing conditions were investigated at ambient and high pressures. One sample was…
Recently, robustness of superconductivity (transition temperature, Tc) under high pressures has been observed in high-entropy alloy (HEA), bcc-type Ti-Zr-Hf-Nb-Ta, and HEA-type compounds (Ag,In,Sn,Pb,Bi)Te with a NaCl-type structure. Since…
The in-plane resistivity $\rho$ and thermal conductivity $\kappa$ of FeAs-based superconductor KFe$_2$As$_2$ single crystal were measured down to 50 mK. We observe non-Fermi-liquid behavior $\rho(T) \sim T^{1.5}$ at $H_{c_2}$ = 5 T, and the…
We report the synthesis and physical property characterization of PrFe1-xCoxAsO with x = 0.0 to 1.0. The studied samples are synthesized by solid state reaction route via vacuum encapsulation method. The pristine compound PrFeAsO does not…
We report the superconductivity at above 30 K in a new FeSe-layer compound K0.8Fe2Se2 (nominal composition) achieved by metal K intercalating in between FeSe layers. It is isostructural to BaFe2As2 and possesses the highest Tc for…
Since the discovery of superconductivity\cite{1} at 26 K in oxy-pnictide $LaFeAsO_{1-x}F_x$, enormous interests have been stimulated in the fields of condensed matter physics and material sciences. Among the five different structures in…
Energetic ion irradiation usually decreases superconducting critical temperature(Tc), with the few exceptions involving increases up to a few K only. However, our recent 2.5X10^15 Ar/cm2 irradiations by 1.5 MeV Ar6+ enhanced Tc of the…
We report on structural, magnetic, conductivity, and thermodynamic studies of FeSe$_{0.5}$Te$_{0.5}$ single crystals grown by self-flux and Bridgman methods. The samples were prepared from starting materials of different purity at various…
The recently discovered (Li${_{1-x}}$Fe${_x}$)OHFeSe superconductor with $T_c$ about 40K provides a good platform for investigating the magnetization and electrical transport properties of FeSe-based superconductors. By using a hydrothermal…
The discovery of high-temperature (Tc) superconductivity in monolayer FeSe on SrTiO3 raised a fundamental question whether high Tc is commonly realized in monolayer iron-based superconductors. Tetragonal FeS is a key material to resolve…
The superconducting gap in FeAs-based superconductor SmFeAs(O1-xFx) (x = 0.15 and 0.30) and the temperature dependence of the sample with x = 0.15 have been measured by Andreev reflection spectroscopy. The intrinsic superconducting gap is…
The finding of superconductivity in Ba0.6K0.4Fe2As2 put the attention on the investigation of compounds that crystallize with ThCr2Si2 structure type such as AT2X2 (A = alkali/ alkaline earth/ rare earth element; T = transition metal and X…
We report the results of $^{77}$Se--nuclear magnetic resonance (NMR) in $\alpha$-FeSe, which exhibits a similar crystal structure to the LaFeAsO$_{1-x}$F$_x$ superconductor and shows superconductivity at 8 K. The nuclear-spin lattice…
The observation of non-bulk superconductivity with an unexpectedly high onset transition temperature Tc up to ~ 49 K in non-superconducting single crystalline CaFe2As2 upon rare-earth doping has raised interesting questions concerning its…