Related papers: Superconductivity up to 29 K in SrFe2As2 and BaFe2…
Electrical resistivity under high pressure have been measured on nominally pure SrFe2As2 up to 14 GPa. The resistivity drop appeared with increasing pressure, and we clearly observed zero resistivity. The maximum of superconducting…
High-pressure electrical resistance measurements have been performed on single crystal Ba0.5Sr0.5Fe2As2 platelets to pressures of 16 GPa and temperatures down to 10 K using designer diamond anvils under quasi-hydrostatic conditions with an…
Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1-xKxFe2As2, which is the maximum found thus far among the 122 phases.…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
We report resistivity measurement under pressure in single crystals of SrFe_2As_2, which is one of the parent materials of Fe-based superconductors. The structural and antiferromagnetic (AFM) transition of T_0 = 198 K at ambient pressure is…
The recently discovered FeAs-based superconductors are a new, promising set of materials for both technological as well as basic research. They offer transition temperatures as high as 55 K as well as essentially isotropic and extremely…
EuFe2As2 is a member of the ternary iron arsenide family. Similar to BaFe2As2 and SrFe2As2, EuFe2As2 exhibits a clear anomaly in resistivity near 200 K. It suggests that EuFe2As2 is another promising parent compound in which…
A new hight Tc Fe-based compound system, AFe2As2 with A = K, Cs, K/Sr and Cs/Sr has been found. Through electron-doping, Tc of the A = K and Cs compounds rises to ~37 K, and finally enter a spin-density-wave state (SDW) through further…
We report pressure-induced superconductivity in a single crystal of CaFe2As2. At atmospheric pressure, this material is antiferromagnetic below 170 K but under an applied pressure of 0.69 GPa becomes superconducting, with a transition…
CaFe$_2$As$_2$ has been found to be exceptionally sensitive to the application of hydrostatic pressure and superconductivity has been found to exist in a narrow pressure region that appears to be at the interface between two different phase…
The superconductor Sr4V2O6Fe2As2 with transition temperature at 37.2 K has been fabricated. It has a layered structure with the space group of p4/nmm, and with the lattice constants a = 3.9296Aand c = 15.6732A. The observed large…
A huge enhancement of the superconducting transition temperature Tc was observed in tetragonal FeSe superconductor under high pressure. The onset temperature became as high as 27 K at 1.48 GPa and the pressure coefficient showed a huge…
New iron selenide superconductors by intercalating smaller-sized alkali metals (Li, Na) and alkaline earths using high-temperature routes have been pursued ever since the discovery of superconductivity at about 30 K in KFe2Se2, but all have…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…
We report the superconductivity at above 30 K in a new FeSe-layer compound K0.8Fe2Se2 (nominal composition) achieved by metal K intercalating in between FeSe layers. It is isostructural to BaFe2As2 and possesses the highest Tc for…
The occurrence of bulk superconductivity at ~22 K is reported in polycrystalline samples of BaFe2-xRuxAs2 for nominal Ru content in the range of x=0.75 to 1.125. A systematic suppression of the spin density wave transition temperature…
The recent discovery of superconductivity at 190~K in highly compressed H$_{2}$S is spectacular not only because it sets a record high critical temperature, but because it does so in a material that appears to be, and we argue here that it…
High pressure electrical resistance and x-ray diffraction measurements have been performed on ruthenium-doped Ba(Fe0.9Ru0.1)2As2, up to pressures of 32 GPa and down to temperatures of 10 K, using designer diamond anvils under…
The evolution of pressure induced superconductivity in single crystal as well as polycrystalline samples of BaFe2As2 has been investigated through temperature dependent electrical resistivity studies in 0-7 GPa pressure range. While the…
By substituting the Fe with the 5d-transition metal Ir in SrFe2As2, we have successfully synthesized the superconductor SrFe2-xIrxAs2 with Tc = 22.3 K at x = 0.5. X-ray diffraction indicates that the material has formed the ThCr2Si2-type…