Related papers: Enhancement of Jc by Hf -Doping in the Superconduc…

Transport critical current (Ic) was measured for MgB2/Fe round wires, with magnetic field oriented perpendicular to the wire and parallel to it. Measurements were made on a wire with pure MgB2 core and another wire where MgB2 core was doped…

Tremendous efforts towards improvement in the critical current density (Jc) of iron based superconductors (FeSCs), especially at relatively low temperatures and magnetic fields, have been made so far through different methods, resulting in…

A comprehensive study of the effects of carbohydrate doping on the superconductivity of MgB2 has been conducted. In accordance with the dual reaction model, more carbon substitution is achieved at lower sintering temperature. As the…

In high-quality c-axis-oriented MgB2 thin films, we observed high critical current densities (Jc) of 16 MA/cm^2 at 15 K under self fields comparable to those of cuprate high-temperature superconductors. The extrapolated value of Jc at 5 K…

We present measurements of the superconducting upper critical field Hc2(T) and the magnetic phase diagram of the superconductor ErNi2B2C made with a scanning tunneling microscope (STM). The magnetic field was applied in the basal plane of…

Polycrystalline MgB2-nDx (x= 0 to 0.1) samples are synthesized by solid-state route with ingredients of Mg, B and n-Diamond. The results from magneto-transport and magnetization of nano-diamond doped MgB2-nDx are reported. Superconducting…

Here we present the magnetic properties and upper critical field (BC2) of polycrystalline Y(Ba1-xSrx)2Cu3O7-{\delta} superconductors, which are being determined through detailed ac/dc susceptibility and resistivity under magnetic field…

The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…

The nano-SiC doped MgB2/Fe wires were fabricated using a powder-in-tube method and an in-situ reaction process. The depression of Tc with increasing SiC doping level remained rather small due to the counterbalanced effect of Si and C…

MgB2-diamond nanocomposite superconductors have been synthesized by addition of nano-diamond powder. Microstructural analysis shows that the nanocomposite superconductor consists of tightly-packed MgB2 nano-grains (~50-100 nm) with…

We present magnetisation data on crystalline and polycrystalline MgB2 before and after irradiation with ~1MeV protons. In the virgin crystal the critical current density is below our noise floor of 103A/cm2 over most of the field range.…

The critical current density has been measured on single crystals of Ru substituted BaFe2As2 superconductor at several temperatures and in fields up to 16 T. The magnetisation versus field isotherms reveal the occurrence of a clear second…

The high resistivity of many bulk and film samples of MgB2 is most readily explained by the suggestion that only a fraction of the cross-sectional area of the samples is effectively carrying current. Hence the supercurrent (Jc) in such…

The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD…

Studies on the new MgB2 superconductor, with a critical temperature Tc ~ 39 K, have evidenced its potential for applications although intense magnetic relaxation effects limit the critical current density, Jc, at high magnetic fields. This…

The addition of artificial pinning centers has led to an impressive increase in critical current density ($J_{\rm c}$) in a superconductor, enabling record-breaking all-superconducting magnets and other applications. $J_{\rm c}$ has reached…

Microstructura lly clean, isov alently P-doped BaFe2As2 (Ba-122) single crystalline thin films have been prepared on MgO (001) substrates by molecular beam epitaxy. These films show a superconducting transition temperature (Tc) of over 30 K…

Nanocarbon-doped Fe-sheathed MgB2 tapes with different doping levels were prepared by the in situ powder-in-tube method. Compared to the undoped tapes, Jc for all the C-doped samples was enhanced by more than an order of magnitude in…

Nb3Sn conductors are important candidates for high-field magnets for particle accelerators, and they continue to be widely used for many laboratory and NMR magnets. However, the critical current density, Jc, of present Nb3Sn conductors…

Transport critical current (Ic) was measured for Fe-sheathed MgB2 round wires. A critical current density of 5.3 x 10^4 A/cm^2 was obtained at 32K. Strong magnetic shielding by the iron sheath was observed, resulting in a decrease in Ic by…