Materials failure in 3D still poses basic challenges. We study 3D brittle crack dynamics using a phase-field approach, where Gaussian quenched disorder in the fracture energy is incorporated. Disorder is characterized by a correlation…
Material failure is mediated by the propagation of cracks, which in realistic 3D materials typically involve multiple coexisting fracture planes. Multiple fracture-plane interactions create poorly understood out-of-plane crack structures,…
We study how the loading rate, specimen geometry and microstructural texture select the dynamics of a crack moving through an heterogeneous elastic material in the quasi-static approximation. We find a transition, fully controlled by two…
To clarify effects of crack speed and cross-link density on fracture energy of acrylamide gels, we evaluated the roughness of the fracture surface and measured the fracture energy taking into account the roughness. The fracture energy…
This paper investigates the effects of plasticity on the effective fracture toughness. A layered material is considered as a modelling system. An elastic-plastic phase-field model and a surfing boundary condition are used to study how the…
Fracture toughness is the material property characterizing resistance to failure. Predicting its value from the solid structure at the atomistic scale remains elusive, even in the simplest situations of brittle fracture. We report here…
Using an elastostatic description of crack growth based on the Griffith criterion and the principle of local symmetry, we present a stochastic model describing the propagation of a crack tip in a 2D heterogeneous brittle material. The model…
The fracture toughness for a mode I/II crack propagating in a ductile material has been subject to numerous investigations. However, the influence of the material hardening law has received very limited attention, with isotropic hardening…
Statistics and thermally activated dynamics of crack nucleation and propagation in a two-dimensional heterogeneous material containing quenched randomly distributed defects are studied theoretically. Using the generalized Griffith criterion…
When fast cracks become unstable to microscopic branching (micro-branching), fracture no longer occurs in an effective 2D medium. We follow in-plane crack front dynamics via real-time measurements in brittle gels as micro-branching unfolds…
The pattern development of multiple cracks in extremely anisotropic solids such as bilayer or multilayer two-dimensional (2D) crystals contains rich physics, which, however, remains largely unexplored. We studied crack interaction across…
Fracture propagation is highly sensitive to the conditions at the crack tip. In heterogeneous materials, microscale obstacles can cause propagation instabilities. Macroscopic heterogeneities modify the stress field over scales larger than…
We have carried out systematic fracture experiments in a single edge notch geometry over a range of stretch rates on dual crosslink hydrogels made from polyvinyl alcohol chains chemically crosslinked with glutaraldehyde and physically…
We study anomalous scaling and multiscaling of two-dimensional crack profiles in the random fuse model using both periodic and open boundary conditions. Our large scale and extensively sampled numerical results reveal the importance of…
We present a gradient-based theoretical framework for predicting hydrogen assisted fracture in elastic-plastic solids. The novelty of the model lies in the combination of: (i) stress-assisted diffusion of solute species, (ii) strain…
Fractal patterns are observed in computational mechanics of elastic-plastic transitions in two models of linear elastic/perfectly-plastic random heterogeneous materials: (1) a composite made of locally isotropic grains with weak random…
Spontaneous material shape changes, such as swelling, growth or thermal expansion, can be used to trigger dramatic elastic instabilities in thin shells. These instabilities originate in geometric incompatibility between the preferred…
We study experimentally the fracture mechanisms of a model cohesive granular medium consisting of glass beads held together by solidified polymer bridges. The elastic response of this material can be controlled by changing the cross-linking…
We characterize the grain boundary (GB) susceptibility to hydrogen-assisted intergranular cracking in pure nickel as a function of coincident site lattice value ($\Sigma$-n), over a wide range of hydrogen concentrations (4 to 14 wppm).…
Crack growth is the basic mechanism leading to the failure of brittle materials. Engineering addresses this problem within the framework of continuum mechanics, which links deterministically the crack motion to the applied loading. Such an…