Related papers: Structural and Superconducting Properties of RbOs2…
Single crystals of KOs2O6 have been grown in a sealed quartz ampoule. Detailed single crystal X-ray diffraction studies at room temperature show Bragg peaks that violate Fd-3m symmetry. With a comparative structure refinement the structure…
The superconducting properties of two beta-pyrochlore oxides, CsOs2O6 and RbOs2O6, are studied by thermodynamic and transport measurements using high-quality single crystals. It is shown that the character of superconductivity changes…
Rattling-induced superconductivity in the beta-pyrochlore oxide RbOs2O6 is investigated under high pressures up to 6 GPa. Resistivity measurements in a high-quality single crystal show that the superconducting transition temperature Tc…
R(O,F)BiS2 (R: La, Ce, Pr, Nd) superconducting single crystals with different F concentrations are grown using a CsCl/KCl flux. The obtained 1-2 mm-sized single crystals have a plate-like shape and are cleavable along the ab-plane. The…
We report the basic thermodynamic properties of the new geometrically frustrated beta-pyrochlore bulk superconductor RbOs2O6 with a critical temperature Tc = 6.4 K. Specific heat measurements are performed in magnetic fields up to 12 T. The…
The synthesis and crystallography, magnetic susceptibility chi, magnetization M, specific heat Cp, in-plane electrical resistivity rho and in-plane magnetic penetration depth measurements are reported for single crystals of APd2As2 (A = Ca,…
Here we report the preparation and superconductivity of the 133-type Cr-based quasi-one-dimensional (Q1D) RbCr3As3 single crystals. The samples were prepared by the deintercalation of Rb+ ions from the 233-type Rb2Cr3As3 crystals which were…
We report the growth and physical properties of single-crystalline Bi$_2$Ta$_3$S$_6$ crystallizing in $P6_3/mcm$ space group, which comprises alternating Ta-S layers and Bi layers with each Bi atom connected with adjacent S atoms.…
Rattling-induced superconductivity in the {\beta}-pyrochlore oxide KOs2O6 is investigated under high pressure up to 5 GPa. Resistivity measurements in a high-quality single crystal reveal a gradual decrease in the superconducting transition…
RbOs2O6, the third superconducting pyrochlore oxide (known so far), has been synthesized by encapsulation and by high pressure techniques. Suitable post chemical treatment of the as-prepared sample allowed us to eliminate the impurity…
We report the discovery of a new pyrochlore oxide superconductor RbOs2O6. The compound crystallizes in the same beta-pyrochlore structure as the recently discovered superconductor KOs2O6, where Os atoms form a corner-sharing tetrahedral…
{\ss}-pyrochore KOs2O6, which shows superconductivity below ~ 9.7K, has been converted into KxOs2O6 (x < 2/3 - 1/2) electrochemically to show spin glass-like behavior below ~ 6.1K. Room temperature sample surface potential versus charge…
F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of…
We present evidence of type I superconductivity in YbSb2 single crystals, from DC and AC magnetization, heat capacity and resistivity measurements. The critical temperature and critical field are determined to be $T_c\approx$ 1.3 K and…
The in-plane thermal conductivity of iron-based superconductor RbFe$_2$As$_2$ single crystal ($T_c \approx$ 2.1 K) was measured down to 100 mK. In zero field, the observation of a significant residual linear term $\kappa_0/T$ = 0.65 mW…
Systematic microwave surface impedance measurements of YBCO single crystals grown in $BaZrO_3$ crucibles reveal new properties that are not directly seen in similar measurements of other YBCO samples. Two key observations obtained from…
We report the results of 87Rb NMR measurements on RbOs2O6, a new member of the family of the superconducting pyrochlore-type oxides with a critical temperature Tc = 6.4 K. In the normal state, the nuclear spin-lattice relaxation time T1…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
The low-temperature specific heat (SH) of overdoped La_{2-x}Sr_{x}CuO_{4} single crystals (0.178=<x=<0.290) has been measured. For the superconducting samples (0.178=<x=<0.238), the derived gap values (without any adjusting parameters)…
The newly discovered superconductors A2Cr3As3 (A = K, Rb, Cs), with a quasi-one-dimensional crystal structure have attracted considerable interest. The crystal structure consists of double-walled tubes of [Cr3As3]^(2-) that extend along the…