Thin films of Co-TiO2 are deposited on silicon and quartz substrates using Pulse Laser Deposition (PLD) process at various oxygen partial pressures ranging from 6.6 x 10-3 Pascals (Pa) to 53 Pa. Crystal structure, transport and magnetic…
Epitaxial LaRh1/2Mn1/2O3 thin films have been grown on (001)-oriented LaAlO3 and SrTiO3 substrates using pulsed laser deposition. The optimized thin film samples are semiconducting and ferromagnetic with a Curie temperature close to 100 K,…
We have carried out extensive comparative studies of the structural and transport properties of CaRuO$_3$ thin films grown under various oxygen pressure. We find that the preferred orientation and surface roughness of the films are strongly…
Thin films of Co2MnSi have been grown on a-plane sapphire substrates from three elemental targets by dc magnetron co-sputtering. These films are single phase, have a strong (110) texture and a saturation magnetization of 4.95 uB/formula…
Thin films of HfO2 doped with 4% La were fabricated on LSMO/STO (100) substrates using pulsed laser deposition. The stability of the ferroelectric orthorhombic phase in the hafnia films was investigated with respect to varying oxygen…
The synthesis of the photochromic YHO films is based on the oxidation of deposited yttrium hydride in ambient conditions. The actual state of the films during the deposition process, which is influenced by the deposition pressure and the…
Entropy stabilization has garnered significant attention as a new approach to designing novel materials. Much of the work in this area has focused on bulk ceramic processing, leaving entropy-stabilized thin films relatively underexplored.…
We report the deposition of thin Co$_2$FeSi films by RF magnetron sputtering. Epitaxial (100)-oriented and L2$_1$ ordered growth is observed for films grown on MgO(100) substrates. (110)-oriented films on Al$_2$O$_3$(110) show several…
Room temperature ferromagnetism was observed in n-type Fe-doped In2O3 thin films deposited on c-cut sapphire substrates by pulsed laser deposition. Structure, magnetism, composition, and transport studies indicated that Fe occupied the In…
High quality vanadium sesquioxide V2O3 films (170-1100 {\AA}) were grown using the pulsed laser deposition technique on (0001)-oriented sapphire substrates, and the effects of film thickness on the lattice strain and electronic properties…
With pulsed laser deposition we have grown c-axis oriented thin films of the nominal composition LaMnO$_{3}$ (LMO) on LSAT(001) substrates. We find that, depending on the oxygen background pressure during growth, the LMO films contain…
TiO$_{2-\delta}$ films were deposited on (100) Lanthanum aluminates LaAlO$_{3}$ substrates at a very low oxygen chamber pressure $P\approx 0.3$ mtorr employing a pulsed laser ablation deposition technique. In previous work, it was…
In the present work, HfO2 thin film (100nm) has been deposited by sputtering technique and annealed at various temperatures ranging from 400 to 1000\degree (in step of 200 \degree) in O2 ambient for 10 min. The samples have been…
Low resistivity (~3-24 mOhm.cm) with tunable n- and p-type phase pure Cu2O thin films have been grown by pulsed laser deposition at 25-200 0C by varying the background oxygen partial pressure (O2pp). Capacitance data obtained by…
We report the growth of undoped and Fe (2 and 5 at. percentage) doped molybdenum oxide thin films on c-plane of sapphire substrate using pulsed laser ablation. X-ray diffraction results show that the films are oriented in (100) direction…
Thin films of the charge-ordered (CO) compound Pr$_{0.5}$Ca$_{0.5}$MnO$_{3}$ have been deposited onto (100)-oriented SrTiO$_{3}$ substrates using the Pulsed Laser Deposition technique. Magnetization and transport properties are measured…
Highly oriented VO2 thin films were grown on sapphire substrates by the sol-gel method that includes a low pressure annealing in an oxygen atmosphere. This reduction process effectively promotes the formation of the VO2 phase over a…
We report on the magnetic and structural properties of ferromagnetic-insulating La$_2$CoMnO$_6$ thin films grown on top of (001) STO substrates by means of RF sputtering technique. Careful structural analysis, by using synchrotron X-ray…
We have investigated the initial growth behavior and resulting microstructural properties of heteroepitaxial ZnO thin films prepared by pulsed laser deposition on sapphire (0001) substrates. High-resolution x-ray diffraction and…
We report on the electrical properties of polycrystalline NbO2 thin film vertical devices grown on TiN coated SiO2/Si substrates using pulsed laser deposition. First, we analyzed the thickness and contact size dependences of threshold…