In this work, the feasibility condition of Powder-In-Tube (PIT) processed wires of Fe(Se,Te) superconductor has been investigated. We faced several technical issues that are extensively described and discussed. In particular, we tested…
Monofilamentary MgB2-wires with a mechanical tough Nb/Cu/steel or Fe/steel sheath were prepared and characterized. The steel content was varied to investigate the reinforcement effect and the consequences for the superconducting properties…
We report the fabrication of small (Ba,A)Fe2As2 (A: Na, K) coils using 10 m-class long round wires, fabricated by powder-in-tube (PIT) method. Coils are sintered using hot-isostatic-press (HIP) technique after glass-fiber insulations are…
Nb-sheathed Sr0.6K0.4Fe2As2 superconducting wires have been fabricated using the powder-in-tube (PIT) method for the first time and the superconducting properties of the wires have been investigated. The transition temperature (Tc) of the…
Superconducting thin films have been prepared in a two-step in-situ process, using the Mg-B plasma generated by pulsed laser ablation. The target was composed of a mixture of Mg and MgB2 powders to compensate for the volatility of Mg and…
Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in…
We demonstrate that good superconductor/insulator/normal-metal tunnel junctions can be fabricated on as-grown superconducting MgB2 thin films. The as-grown films were prepared by coevaporation at low growth temperatures of around 280deg.…
The new superconductor MgB2 may prove useful for microwave applications at intermediate temperatures. MgB2 films with the thickness of 300 - 400 nm have surface resistance Rs less than 0.01 mOhms at a frequency (f) of 8.5 GHz and 7 K,and ~…
In this letter, we report the results of transport Jc of solenoid coils upto 100 turns fabricated with Cu-sheathed MgB2 wires using a wind-reaction in-situ technique. Despite the low density of single core and some reaction between Mg and…
The polycrystalline Mn1.26Fe0.60P0.48Si0.52 microwires were successfully fabricated for the first time by the melt-extraction technique, and their magnetic and magnetocaloric properties were investigated systematically. The structural…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
Polycrystalline MgB2 samples with 10 wt % silicon powder addition were prepared by an in-situ reaction process. Two different Si powders, one with coarse (44 mm) and the other with nano-size (<100 nm) particles were used for making samples.…
Ex-situ Powder-In-Tube MgB2 tapes prepared with ball-milled, undoped powders showed a strong enhancement of the irreversibility field H*, the upper critical field Hc2 and the critical current density Jc(H) together with the suppression of…
We report the successful manufacture and characterization of a microwave resonant cylindrical cavity made of bulk MgB2 superconductor (Tc = 38.5 K), which has been produced by the Reactive Liquid Mg Infiltration technique. The quality…
Fe-sheathed MgB2 tapes with cheap stearic acid, Mg stearate and Zn stearate doping were prepared through the in situ powder-in-tube method. It is found that Jc, Hirr, and Hc2 were significantly enhanced by doping. Compared to the pure…
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient…
0.5 to 5.0 wt.% Dy2O3 was in-situ reacted with Mg + B to form pinned MgB2. While Tc remained largely unchanged, Jc was strongly enhanced. The best sample (only 0.5 wt.% Dy2O3) had a Jc of 6.5 x 10^5 A/cm^2 at 6K, 1T and 3.5 x 10^5 A/cm^2 at…
In this work we investigate the effect of each different heat treatment stage in the fabrication of Bi2Sr2CaCu2O8+d superconducting wires on intra-grain and inter-grain superconducting properties. We measure magnetic critical temperature Tc…
We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The…
The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing…