Related papers: Effect of Rb and Cs-doping on superconducting prop…
The electronic anisotropy in MgB2, is still a not completely clear topic; high quality c-oriented films are suitable systems to investigate this property. In this work we present our results on MgB2 superconducting thin films grown on MgO…
We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…
The effects of Mg deficiency in MgB2 films grown by using hybrid physical-chemical vapor deposition were investigated after vacuum annealing at various temperatures. High-quality MgB2 films grown on c-cut Al2O3 substrates with different…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
This paper presents a brief review on the reported anisotropic properties of MgB2, in the superconducting state (e.g. upper critical field Hc2, field penetration depth, coherence length, energy gap) as well as in the normal state (e.g.,…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
MgB2 thin films were deposited using Pulsed Laser Deposition (PLD) and ex-situ annealing in Mg atmosphere. The films presented critical temperatures up to 36K and turned out to be preferentially c-oriented both on Al2O3 (r-cut) and MgO(100)…
The effect of damage induced by 2-MeV alpha particles, followed by annealing, on the critical temperature (Tc), resistivity, and upper critical field (Hc2), of three MgB2 films made by different deposition processes has been studied. Damage…
We report measurements of the ab-plane superfluid density Ns (magnetic penetration depth, \lambda) of severely underdoped films of YBa2Cu3O6+x, with Tc's from 6 to 50 K. Tc is not proportional to Ns(0); instead, we find Tc ~ Ns^{1/2.3 +/-…
The amount of oxygen incorporated into MgB2 thin films upon exposure to atmospheric gasses is found to depend strongly on the material's stoichiometry. Rutherford backscattering spectroscopy was used to monitor changes in oxygen…
Oxygen was systematically incorporated in MBE grown MgB2 films using in-situ post-growth anneals in an oxygen environment. Connectivity analysis in combination with measurements of the critical temperature and resistivity indicate that…
We investigate the influence of carbon-ion irradiation on the superconducting critical properties of MgB$_2$ thin films. MgB$_2$ films of two thicknesses viz. 400 nm (MB400nm) and 800 nm (MB800nm) were irradiated by 350 keV C ions having a…
The new superconductor MgB2 may prove useful for microwave applications at intermediate temperatures. MgB2 films with the thickness of 300 - 400 nm have surface resistance Rs less than 0.01 mOhms at a frequency (f) of 8.5 GHz and 7 K,and ~…
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS).…
Angular-dependent channeling Rutherford Backscattering Spectroscopy (c-RBS) has been used to quantify the fraction of Cr atoms on substitutional, interstitial, and random sites in epitaxial Ga1-xCrxN films grown by reactive molecular-beam…
We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…
The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron…
We have studied the effect of damage induced by 2-MeV alpha particles on the critical temperature, Tc, and resistivity of MgB2 thin films. This technique allows defects to be controllably introduced into MgB2 in small successive steps. Tc…
The high resistivity of many bulk and film samples of MgB2 is most readily explained by the suggestion that only a fraction of the cross-sectional area of the samples is effectively carrying current. Hence the supercurrent (Jc) in such…
Thin films of the high-temperature superconductor HgBa$_2$CaCu$_2$O$_{6+\delta}$ have been prepared on SrTiO$_3$ substrates by pulsed-laser deposition of precursor films and subsequent annealing in mercury-vapor atmosphere. The…