Bulk samples of (Sn1−xSbxO2−δ) with x = 0.00, 0.10, 0.20, 0.30 are synthesized by solid-state reaction route. Samples were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and UV-Vis spectroscopy. The x-ray diffraction patterns indicate that the gross structure/phase of (Sn1−xSbxO2−δ) do not change with the substitution of antimony (Sb) up to x = 0.30. The surface morphological examination with SEM revealed the fact that the grain size in the antimony doped sample is larger than that of undoped one and hence pores/voids between the grains increase with Sb concentration up to 0.30. TEM image of undoped sample indicates that the SnO2 grains have diameters ranging from 25 to 120 nm and most grains are in cubic or spherical shape. As antimony content increases, the nanocubes/spheres are converted into microcubes/spheres. The reflectance of Sn1−xSbxO2−δ samples increases whereas absorbance of these samples decreases with the increased concentration of antimony (Sb) for the wavelength range 360 - 800 nm. The energy bandgap of Sb doped - SnO2 samples were obtained from optical absorption spectra by UV-Vis absorption spectroscopy. Upon increasing the Sb concentration the bandgap of the samples was found to increase from 3.367 eV to 3.558 eV.
@article{arxiv.1107.1807,
title = {Synthesis and structural/microstructural characteristics of antimony doped tin oxide $(Sn_{1-x}Sb_{x}O_{2-\delta})$},
author = {Rita Singh and Sushant Gupta and B. Das},
journal= {arXiv preprint arXiv:1107.1807},
year = {2015}
}